ANÁLISE TERMOGRAVIMÉTRICA DO SISTEMA SIC-AL2O3-Y2O3 EM BAIXAS TEMPERATURAS

THERMOGRAVIMETRIC ANALYSIS OF THE SIC-AL2O3-Y2O3 SYSTEM AT LOW TEMPERATURES

Authorship

ALKIMIM, HELLEN KARINA PEREIRA; COSTA, RHAYANA AYAMY YAMAGUCHI GOMES DA; CARVALHO, MAGNO TORRES; SOUZA, RODRIGO FERNANDES M. DE; CAMPOS, JOSÉ BRANT DE; LIMA, EDUARDO DE SOUSA

ALKIMIM, HELLEN KARINA PEREIRA

I am this author

COSTA, RHAYANA AYAMY YAMAGUCHI GOMES DA

I am this author

CARVALHO, MAGNO TORRES

I am this author

SOUZA, RODRIGO FERNANDES M. DE

I am this author

CAMPOS, JOSÉ BRANT DE

I am this author

LIMA, EDUARDO DE SOUSA

I am this author

DOI

10.5151/2594-5327-41252

Downloads

Abstract

A PERDA DE MASSA é UM FENôMENO CONHECIDO NA SINTERIZAçãO DO CARBETO DE SILíCIO (SIC) SINTERIZADO VIA FASE LíQUIDA, O QUE COMPROMETE COMPROMETENDO SUAS PROPRIEDADES TERMO-MECâNICAS. O OBJETIVO DESTE TRABALHO é ESTUDAR A ALTERAçãO DE MASSA DO CARBETO EM BAIXAS TEMPERATURAS NA PRESENçA DE SEUS ADITIVOS MAIS USUAIS, ANTES DO INíCIO DA SINTERIZAçãO. FORAM PREPARADAS COMPOSIçõES DE SIC COM ALUMINA, SIC COM íTRIA E COM OS 3 COMPOSTOS SIMULTANEAMENTE. O SIC PURO FOI USADO COMO REFERêNCIA. FORAM REALIZADAS ANáLISES TERMOGRAVIMéTRICAS ATé 600ºC, EM ATMOSFERA DE ARGôNIO, MICROSCOPIA ELETRôNICA DE VARREDURA (MEV), DIFRAçãO DE RAIOS X (DRX) E MEDIDAS DE MASSA. O SIC APRESENTA GANHO DE MASSA POUCO EXPRESSIVA A APROXIMADAMENTE 900ºC. O SIC COM ADIçãO DE AL2O3 E Y2O3 TAMBéM APRESENTA UM GANHO POUCO EXPRESSIVA, O QUE PODERá INDICAR UMA PROVáVEL OXIDAçãO DO SIC SEGUNDO A LITERATURA.

MASS LOSS IS A KNOWN PHENOMENON IN SILICON CARBIDE (SIC) SINTERED VIA LIQUID PHASE, WHICH COMPROMISES COMPROMISING ITS THERMO-MECHANICAL PROPERTIES. THE OBJECTIVE OF THIS WORK IS TO STUDY THE MASS CHANGE OF CARBIDE AT LOW TEMPERATURES IN THE PRESENCE OF ITS MOST USUAL ADDITIVES BEFORE THE BEGINNING OF SINTERING. SIC COMPOSITIONS WITH ALUMINA, SIC WITH ITTRY AND THE 3 COMPOUNDS SIMULTANEOUSLY WERE PREPARED. PURE SIC WAS USED AS A REFERENCE. THERMOGRAVIMETRIC ANALYZES UP TO 600ºC WERE PERFORMED IN ARGON ATMOSPHERE, SCANNING ELECTRONIC MICROSCOPY (MEV), X-RAY DIFFRACTION (DRX) AND MASS MEASUREMENTS. THE SIC HAS LITTLE EXPRESSIVE MASS GAIN AT APPROXIMATELY 900ºC. SIC WITH THE ADDITION OF AL2O3 AND Y2O3 ALSO HAS AN UNCOMPOSED GAIN, WHICH MAY INDICATE PROBABLE SIC OXIDATION ACCORDING TO THE LITERATURE.

Keywords

SiC; Al2O3; Y2O3; Ganho de massa

SiC; Al2O3; Y2O3; Mass gain.