ANÁLISE TÉRMICA DE DILATOMETRIA DE COMPÓSITOS DE MATRIZ EPÓXI REFORÇADOS POR FIBRA DE CIPÓ TITICA

THERMAL ANALYSIS OF DILATOMETRY OF EPOXY MATRIX COMPOSITES REINFORCED BY TITTIC VINE FIBER

Authorship

COSME, GRAZIELE MEDEIROS; DELAQUA, GEOVANA CARLA GIRONDI; LOPEZ, FELIPE PERISSÉ DUARTE; SIMONASSI, NOAN TONINI; MONTEIRO, SERGIO NEVES

COSME, GRAZIELE MEDEIROS

I am this author

DELAQUA, GEOVANA CARLA GIRONDI

I am this author

LOPEZ, FELIPE PERISSÉ DUARTE

I am this author

SIMONASSI, NOAN TONINI

I am this author

MONTEIRO, SERGIO NEVES

I am this author

DOI

10.5151/2594-5327-40534

Downloads

Abstract

DEVIDO A URGENTE NECESSIDADE POR PRODUTOS MAIS SUSTENTáVEIS E AMIGOS DO MEIO AMBIENTE, AS FIBRAS SINTéTICAS ESTãO SENDO CADA VEZ MAIS SUBSTITUíDAS POR FIBRAS DE FONTES VEGETAIS, COMO REFORçO EM COMPóSITOS DE MATRIZ POLIMéRICA. ESSES COMPóSITOS POSSUEM DIVERSOS TIPOS DE APLICAçõES, COMO POR EXEMPLO, NA ENGENHARIA CIVIL, NA INDúSTRIA DE ESPORTES, NO SETOR MILITAR ETC. DEVIDO AO USO DA FIBRA NATURAL COMO REFORçO, ESSE COMPóSITO APRESENTA UMA CERTA INSTABILIDADE EM SUAS PROPRIEDADES TERMOMECâNICAS, QUANDO SUJEITOS/EXPOSTOS AO AQUECIMENTO E RESFRIAMENTO, DEVIDO A ESSA INSTABILIDADE é PRECISO INVESTIGAR TAIS PROPRIEDADES ANTES DE SUA EFETIVA APLICAçãO NA INDúSTRIA. LOGO é NECESSáRIO UMA SéRIE DE CARACTERIZAçõES TéRMICAS, ENTRE ELAS, A DILATOMETRIA QUE é UMA TéCNICA ANALíTICA SIMPLES, SENSíVEL E CONFIáVEL, REALIZADA DE ACORDO COM A NORMA ASTM E 228, A FIM DE DETERMINAR A TEMPERATURA DE TRANSIçãO VíTREA (TG) E COMO A INSERçãO E AUMENTO DA FRAçãO VOLUMéTRICA DE FIBRA ATUA NESSA TG EM UM FAIXA DE TEMPERATURA VARIANDO DA AMBIENTE ATé 200 °C, ONDE NãO OCORRE A DEGRADAçãO DO POLíMERO E NEM DA FIBRA NATURAL E SEUS CONSTITUINTES. LOGO FOI POSSíVEL OBSERVAR QUE A TG DO MATERIAL OCORRE POR VOLTA DOS 50 °C, ONDE FOI POSSíVEL NOTAR UMA RETRAçãO DO MATERIAL COM O AUMENTO DA FRAçãO VOLUMéTRICA DE FIBRA.

DUE TO THE URGENT NEED FOR MORE SUSTAINABLE AND ENVIRONMENTALLY FRIENDLY PRODUCTS, SYNTHETIC FIBERS ARE INCREASINGLY BEING REPLACED BY FIBERS FROM VEGETABLE SOURCES, AS REINFORCEMENT IN POLYMER MATRIX COMPOSITES.THESE COMPOUNDS HAVE DIFFERENT TYPES OF APPLICATIONS, SUCH AS IN ENGINEERING. HOWEVER, DUE TO THE USE OF NATURAL FIBER AS REINFORCEMENT, THIS COMPOSITE PRESENTS A CERTAIN INSTABILITY IN ITS THERMOMECHANICAL PROPERTIES WHEN SUBJECTED/EXPOSED TO HEATING AND COOLING AND DUE TO THIS INSTABILITY IT IS NECESSARY TO INVESTIGATE THESE PROPERTIES BEFORE ITS EFFECTIVE APPLICATION IN INDUSTRY. A SERIES OF THERMAL CHARACTERIZATIONS ARE THEN CARRIED OUT, INCLUDING DILATOMETRY, WHICH IS A SIMPLE, SENSITIVE AND RELIABLE ANALYTICAL TECHNIQUE, CARRIED OUT IN ACCORDANCE WITH THE ASTM E 228 STANDARD, IN ORDER TO DETERMINE THE GLASS TRANSITION TEMPERATURE (TG) AND HOW THE DECREASE AND INCREASE IN THE VOLUMETRIC FRACTION OF FIBER ACTS ON THIS TG IN A TEMPERATURE RANGE RANGING FROM ROOM TEMPERATURE TO 200 °C, WHERE DEGRADATION OF THE POLYMER OR THE NATURAL FIBER AND ITS CONSTITUENTS DOES NOT OCCUR. IT WAS SOON POSSIBLE TO OBSERVE THAT THE TG OF THE MATERIAL OCCURS AT AROUND 50 °C, WHERE IT WAS POSSIBLE TO NOTICE A SHRINKAGE OF THE MATERIAL WITH THE INCREASE IN THE FIBER VOLUME FRACTION.

Keywords

Compósitos; Fibra natural; Cipó titica, Dilatometria.

Composites; Natural fiber; Titica vine, Dilatometry.