AQUISIÇÃO DE ROCHA DE ENGENHARIA PARA APLICAÇÃO NA CONSTRUÇÃO CIVIL

ACQUISITION OF ENGINEERING STONE FOR APPLICATION IN CIVIL CONSTRUCTION

Authorship

Souza, Vitor da Silva de; Costa, Elaine Aparecida Santos Carvalho; Barreto, Gabriela Nunes Sales; Vieira, Carlos Maurício Fontes; Delaqua, Geovana Carla Girondi; Monteiro, Sérgio Neves

DOI

10.5151/2594-5327-34311

Downloads

heading.download_article_detail 32 Downloads

Abstract

COM A ECLOSÃO DOS RESÍDUOS SÓLIDOS PROVENIENTES DE LÂMPADAS FLUORESCENTES NO MEIO AMBIENTE, CONSIDERADAS POLUENTES CONTAMINANTES, AS ROCHAS ARTIFICIAIS SURGEM COMO UM ESCAPE SUSTENTÁVEL PARA COMERCIALIZAÇÃO E RECICLAGEM DESSE MATERIAL AFIM DE EVITAR POLUIÇÕES. O OBJETIVO DO PROJETO É AVALIAR O EFEITO DA INCORPORAÇÃO DO RESÍDUO DE LÂMPADAS FLUORESCENTES PROVENIENTES DA RECICLAGEM EM ROCHAS ARTIFICIAIS COM USO DE UMA MATRIZ POLIMÉRICA AFIM DE ANALISAR, DETERMINAR E AVALIAR AS ROCHAS COM INTENÇÃO DE VERIFICAR A APROVAÇÃO DAS PROPRIEDADES FÍSICAS E MECÂNICAS, PODENDO ASSIM QUANTIFICAR VALORES AO PRODUTO PARA POSSÍVEIS SURGIMENTOS DE STAKEHOLDERS. A METODOLOGIA FOI O PROCESSO “VIBRAÇÃO, COMPRESSÃO E VÁCUO” QUE ATUALMENTE É UTILIZADA PELA INDÚSTRIA DE ROCHA ARTIFICIAL COMPACTADA. NESSE PROCESSO O RESÍDUO FOI MISTURADO COM A RESINA POLIMÉRICA VEGETAL POLIURETANO E POSTERIORMENTE SUBMETIDO A TEMPERATURA DE 80ºC SOB PRESSÃO DE 10TON PROMOVENDO A POLIMERIZAÇÃO. A ROCHA ARTIFICIAL COM RESÍDUO DE LÂMPADA PASSOU POR UM PROCESSO DE CURA E FOI SUBMETIDA AOS TESTES. OS RESULTADOS OBTIDOS PARA A DENSIDADE FORAM DE 2,18G/CM³, POROSIDADE DE 1,84 ± 0,17% E ABSORÇÃO DE ÁGUA 0,84 ± 0,07%. A TENSÃO MÁXIMA DE RUPTURA FOI DE 18,62 MPA E BOA RESISTÊNCIA AO ATAQUE QUÍMICO. O PRODUTO INOVADOR DEMONSTRA SER COMPATÍVEL COM ROCHAS ARTIFICIAIS COMERCIALIZADAS. CONCLUÍSSE QUE A ROCHA PRODUZIDA APRESENTA UMA QUALIDADE MÉDIA, PODENDO SER APLICADA EM ALGUMAS ÁREAS NA CONSTRUÇÃO CIVIL, EM ÁREAS INTERNAS COMO PAREDES, PISOS CONVENCIONAIS E PISOS FLUTUANTES; COM EVENTUAL UTILIZAÇÃO DE ÁGUA.

 

BY THE ECLOSION OF SOLID WASTE FROM FLUORESCENT LAMPS IN THE ENVIRONMENT, CONSIDERED POLLUTANT AND CONTAMINANT, THE ARTIFICIAL STONES ARISE AS A SUSTAINABLE ESCAPE FOR THE COMMERCIALIZATION AND RECYCLING OF THIS MATERIAL SEEKING TO AVOID POLUTION. THE AIM OF THE PROJECT IS TO EVALUATE THE INCORPORATION EFFECT OF FLUORESCENT LAMPS WASTE FROM ARTIFICIAL STONES RECYCLING BY USING A POLYMER MATRIX, LOOKING FOR ANALYZING, DETERMINING AND EVALUATING THE STONES TO VERIFY THE APPROVAL OF MECHANICAL AND PHYSICAL PROPERTIES MAKING IT POSSIBLE TO QUANTIFY VALUES TO THE PRODUCT FOR POSSIBLE EMERGENCE OF STAKEHOLDERS. THE METHODOLOGY USED HAS BEEN THE PROCESS OF ‘’VIBRATION, COMPRESSION AND VACUUM’’ WHICH IS CURRENTLY USED BY THE COMPACTED ARTIFICIAL STONES INDUSTRY. IN THIS PROCESS THE WASTE WAS MIXED WITH VEGETABLE POLYMERIC POLYURETHANE RESIN AND THEN SUBMITTED TO A TEMPERATURE OF 80ºC UNDER THE PRESSURE OF 10TON PROMOTING THE POLYMERIZATION. THE ARTIFICIAL STONE PRODUCED BY WASTE FROM THE LAMP WAS SUBMITTED TO A CURING PROCESS ANDTO TESTS. THE RESULTS OBTAINED FOR THE DENSITY WERE 2.18G/CM³, 1.84 ± 0.17% OF POROSITY AND WATER ABSORPTION OF 0.84 ± 0.07%. THE MAXIMUM TENSION OF RUPTURE WAS 18 MPA, SHOWING A GOOD RESISTANCE TO CHEMICAL ATTACK, AND IT ALSO DEMONSTRATES TO BE COMPATIBLE WITH ARTIFICIAL STONES COMMERCIALIZED. IT IS CONCLUDED THAT THE STONE PRODUCED FEATURES AN AVARAGE QUALITY, AND IT COULD BE APPLIED ON SOME AREAS OF CIVIL CONSTRUCTION, ON INTERNAL AREAS SUCH AS WALLS, CONVENTIONAL FLOORS AND FLOATING FLOORS; WITH EVENTUAL USE OF WATER.

Keywords

Lâmpadas fluorescentes, Rocha Artificial, Resina Natural, Mamona.

Fluorescent lamps, Artificial stone, Natural Resin, Castor oil.