ARGAMASSAS PRODUZIDAS COM AREIA PLÁSTICA CAULINÍTICA: UMA AVALIAÇÃO EXPERIMENTAL

MORTARS PRODUCED WITH KAOLINITE PLASTIC SAND: AN EXPERIMENTAL EVALUATION

Authorship

MARVILA, MARKSSUEL TEIXEIRA; CAIXETA, DOUGLAS MAXWEL CARNEIRO; MARQUES, MARÍLIA GONÇALVES; MESQUITA, LEONARDO CARVALHO; AZEVEDO, AFONSO RANGEL GARCEZ DE

MARVILA, MARKSSUEL TEIXEIRA

I am this author

CAIXETA, DOUGLAS MAXWEL CARNEIRO

I am this author

MARQUES, MARÍLIA GONÇALVES

I am this author

MESQUITA, LEONARDO CARVALHO

I am this author

AZEVEDO, AFONSO RANGEL GARCEZ DE

I am this author

DOI

10.5151/2594-5327-40525

Downloads

Abstract

AS ARGAMASSAS à BASE DE CIMENTO PORTLAND E CAL HIDRATADA SãO AMPLAMENTE UTILIZADAS NA CONSTRUçãO CIVIL PARA REVESTIMENTO E ASSENTAMENTO DE PAREDES, POR EXEMPLO. PORéM, OS AGLOMERANTES UTILIZADOS NA PRODUçãO DE ARGAMASSAS SãO PRODUZIDOS DE FORMA PREJUDICIAL AO MEIO AMBIENTE, EVIDENCIANDO A NECESSIDADE DE LIGANTES ALTERNATIVOS. NESTE TRABALHO FOI AVALIADA A UTILIZAçãO DE AREIA PLáSTICA CAULINíTICA EM ARGAMASSAS, SUBSTITUINDO A CAL HIDRATADA EM TEORES DE 0%, 50% E 100%. FORAM AVALIADAS PROPRIEDADES NO ESTADO FRESCO, COMO CONSISTêNCIA E SQUEEZE FLOW; ALéM DE PROPRIEDADES NO ESTADO ENDURECIDO, COMO RESISTêNCIA à COMPRESSãO, ABSORçãO DE áGUA, DIFRAçãO DE RAIOS X (DRX) E MICROSCOPIA ELETRôNICA DE VARREDURA (MEV). OS TESTES DE TRABALHABILIDADE MOSTRAM QUE A AREIA PLáSTICA DE CAULINITA TEM POTENCIAL PARA MELHORAR A TRABALHABILIDADE DA ARGAMASSA. NOS TESTES DINâMICOS (CONSISTêNCIA) OBSERVOU-SE QUE A COMPOSIçãO DE AREIA PLáSTICA 100% CAULINITA é VIáVEL POIS PROMOVE AUMENTO NO ESPALHAMENTO DE 253 PARA 265 MM. NOS TESTES ESTáTICOS (SQUEEZE FLOW) A COMPOSIçãO COM 50% DE AREIA PLáSTICA CAULINITA APRESENTOU OS MELHORES RESULTADOS DE ESPALHAMENTO, COM VALORES DE 10,7 MM, ENQUANTO AS COMPOSIçõES CONTENDO 0% E 100% APRESENTARAM ESPALHAMENTO DE 8,97 E 7,40 MM, RESPECTIVAMENTE. ISTO DEMONSTRA O POTENCIAL DO USO DE AREIA PLáSTICA DE CAULINITA EM ARGAMASSAS. OS RESULTADOS DO ESTADO ENDURECIDO, COMO RESISTêNCIA à COMPRESSãO E ABSORçãO DE áGUA, TAMBéM FORAM SATISFATóRIOS. POR FIM, OBSERVOU-SE PELOS RESULTADOS DE DRX E MEV QUE A AREIA PLáSTICA CAULINíTICA APRESENTA ADESãO COM OS PRODUTOS DE HIDRATAçãO DO CIMENTO PORTLAND NA ARGAMASSA, PROMOVENDO REDUçãO DE ETRINGITA E PORTLANDITA DEVIDO à SUA MODERADA POZOLANICIDADE. COM BASE NESTES RESULTADOS é POSSíVEL CONCLUIR QUE A AREIA PLáSTICA CAULINíTICA é UM SUBSTITUTO VIáVEL PARA A CAL HIDRATADA EM ARGAMASSAS

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

Keywords

caulinita; areia; argamassa; fluxo de compressão; trabalhabilidade

kaolinite; sand; mortar; squeeze flow; workability.