AVALIAÇÃO MICROESTRUTURAL, TERMOQUÍMICA E MECÂNICA DO COMPORTAMENTO DE PELOTAS AUTORREDUTORAS A BASE DE POEIRA DE ACIARIA ELETRICA CONTENDO ZINCO PARA O PROCESSO WAELZ

EVALUATION MICROSTRUCTURAL, TERMOCHEMISTRY AND MECHANICAL OF BEHAVIOR PELLETS AUTO REDUCING OF ELECTRIC ARC FURNACE DUST CONTANING ZINC FOR WAELZ PROCESS

DOI

10.5151/2594-357X-28110

Downloads

Abstract

Uma grande quantidade de poeiras e fumos contendo óxidos de ferro, zinco, alumínio, cálcio, chumbo, magnésio e cádmio são habitualmente gerados durante a produção do aço em usinas siderúrgicas semiintegradas. Processos hidrometalúrgicos e pirometalúrgicos têm sido desenvolvidos para o tratamento da poeira de aciaria elétrica (PAE). O processo Waelz, que recupera parte destes resíduos por meio de reações metalúrgicas de redução e oxidação em um forno rotativo, é uma tecnologia de destaque empregada para a recuperação dos metais voláteis, e tem sido a mais usada nos últimos 40 anos. Neste trabalho, foi realizado um estudo termodinâmico do processo Waelz, visando à otimização das condições metalúrgicas necessárias para garantir a recuperação dos metais voláteis (em especial zinco), de forma a assegurar a minimização de impactos ambientais e maximização de opções de processamento para a recuperação do zinco contido. As variáveis cinéticas foram estudadas por meio da execução de uma serie de 6 experimentos, englobando os principais fatores do processamento, tais como: tipo de redutor e tempo/temperatura de processamento. Também foi avaliado o comportamento mecânico das pelotas para cada formulação. Caracterizações por meio de microscopia eletrônica com microanálise via EDS, difração de raios X, fluorescência de raios X, análise granulométrica a laser, resistência à compressão, porcentagem de matéria volátil, carbono fixo e cinzas foram empregados.

 

A high amount of residues such as dust and fumes containing iron oxides, zinc, aluminum, calcium, lead, magnesium and cadmium are usually generated during the steel production in steel mills, which produce it from scrap melting. Hydrometallurgical and pyrometallurgical processes have been developed to the treatment of electric arc furnace dust (EAF). The Waelz process, that recovers part of these residues through metallurgical reactions of oxidation and reduction in a rotary kiln, is a leading technology used for the recovery of volatile metals, and has been widely used over the past 40 years. In this work, an initial thermodynamic and kinetic study of the Waelz reduction process was conducted, aiming to optimize the metallurgical conditions needed to ensure the recovery of volatile metals (especially zinc) and therefore assure the minimization of environmental impacts and maximization of more sustainable processing options and with higher added value due to the increase of zinc recovery from the dust and metallurgical residues. Kinetic variables were studied by running a series of six experiments, covering the main processing variables such as content and type of the binder, content and type of the reducer and processing time/temperature. The behavior and thermomechanical properties will also be assessed. There were used characterizations by electron microscopy, X-ray diffraction, X-ray fluorescence, particle size analysis with laser, compressive strength, percentage of volatile matter, fixed carbon and ash were employed.

Keywords

Pelotas autorredutoras, Recuperação do zinco, Tratamento de resíduo de aciaria, Processo Waelz

Self-reduction pellets, Zinc recovery, Steelmaking dust treatment, Waelz process

How to refer

Buitrago, Leidy Julieth Hernández; Beneduce, Flávio; Prada, Ivan Daza; Silva, Guilherme Frederico Bernardo Lenz da. AVALIAÇÃO MICROESTRUTURAL, TERMOQUÍMICA E MECÂNICA DO COMPORTAMENTO DE PELOTAS AUTORREDUTORAS A BASE DE POEIRA DE ACIARIA ELETRICA CONTENDO ZINCO PARA O PROCESSO WAELZ , p. 726-736. In: 46º Seminário de Redução/ 17º Minério de Ferro/ 4º Aglomeração, Rio de Janeiro, 2016.