Title

Avaliação química e estrutural da liga AL- 1% Si com nanotubos de carbono

Chemical and Structural Evaluation of the Al-1% Si Alloy with Carbon Nanotubes

Authorship

SILVA, VICTOR HENRIQUE DA COSTA; ALMEIDA, ANDERSON PEREIRA DE; HOLANDA, LUCAS VINICIUS SANTOS DE; VASCONCELOS, ANGELA DE JESUS; BARROS, ANDRÉ DOS SANTOS; PRAZERES, EMERSON RODRIGUES; COSTA, DEIBSON SILVA DA

SILVA, VICTOR HENRIQUE DA COSTA

I am this author

ALMEIDA, ANDERSON PEREIRA DE

I am this author

HOLANDA, LUCAS VINICIUS SANTOS DE

I am this author

VASCONCELOS, ANGELA DE JESUS

I am this author

BARROS, ANDRÉ DOS SANTOS

I am this author

PRAZERES, EMERSON RODRIGUES

I am this author

COSTA, DEIBSON SILVA DA

I am this author

DOI

10.5151/2594-4711-44125

Downloads

Abstract

Este trabalho avaliou a microestrutura de um nanocompósito de Al-1%Si reforçado com 0,05% em peso de nanotubos de carbono de paredes múltiplas (NTCPM). Amostras fundidas em coquilha foram submetidas à análise macrográfica com reagente Keller e espectroscopia Raman. A macroestrutura revelou um refino de grãos equiaxiais após a introdução dos NTCPM na liga de Al-1%Si. Por fim, a espectroscopia Raman identificou as bandas RBM (106,46 cm⁻¹), D (1345,14 cm⁻¹), G (1582,15 cm⁻¹) e G'(2D) (2687,94 cm⁻¹), com razão ID/IG de 0,94, confirmando nanotubos de baixa pureza. Conclui-se que os NTCPM modificam a liga, refinando eficientemente o grão e alterando quantitativamente a morfologia microestrutural da fratura da liga.

This study evaluated the microstructure of an Al-1%Si nanocomposite reinforced with 0.05 wt.% multi-walled carbon nanotubes (MWCNTs). Chill-cast samples were subjected to macrographic analysis using Keller's reagent, microstructure analysis via scanning electron microscopy (SEM) using ImageJ software, and Raman spectroscopy. The macrostructure revealed equiaxed grain refinement after introducing the MWCNTs into the Al-1%Si alloy. Finally, Raman spectroscopy identified the RBM (106.46 cm⁻¹), D (1345.14 cm⁻¹), G (1582.15 cm⁻¹), and G'(2D) (2687.94 cm⁻¹) bands, with an ID/IG ratio of 0.94, confirming low-purity nanotubes. It is concluded that MWCNTs modify the alloy, efficiently refining the grain and quantitatively altering the microstructural morphology of the alloy's fracture.