Title

AVALIAÇÃO DA EFICIÊNCIA DO LÍQUIDO IÔNICO [BMIM]BF4 COMO INIBIDOR DE CORROSÃO NA JUNTA SOLDADA DO AÇO INOXIDÁVEL DUPLEX UNS S31803 EM SOLUÇÃO DE H2SO4

EVALUATION OF THE EFFICIENCY OF [BMIM]BF4 LIQUID IONIC AS A CORROSION INHIBITOR FOR THE WELDED JOINT OF DUPLEX STAINLESS STEEL UNS S31803 IN H2SO4 SOLUTION

Authorship

LOPES, STHEFANIE DE CARVALHO MENDES; SOUZA, LUCAS MENEZES DE; GADIOLI, ANDERSON OLIVEIRA; AMARAL, THIAGO BARRETO DA SILVA; PEREIRA, ELAINE CRISTINA

LOPES, STHEFANIE DE CARVALHO MENDES

8 Articles, Downloaded 84 Times

SOUZA, LUCAS MENEZES DE

I am this author

GADIOLI, ANDERSON OLIVEIRA

I am this author

AMARAL, THIAGO BARRETO DA SILVA

I am this author

PEREIRA, ELAINE CRISTINA

I am this author

DOI

10.5151/2594-5327-40775

Downloads

Abstract

A INFLUêNCIA DO LíQUIDO IôNICO TETRAFLUOROBORATO DE 1-BUTIL-3-METILIMIDAZóLIO ([BMIM]BF4) NA INIBIçãO DA CORROSãO DA JUNTA SOLDADA E TRATADA TERMICAMENTE DE AçO INOXIDáVEL DUPLEX UNS S31803 EM UMA SOLUçãO DE áCIDO SULFúRICO 1M FOI INVESTIGADA POR MEIO DE TéCNICAS ELETROQUíMICAS. A ANáLISE DA MORFOLOGIA DA SUPERFíCIE FOI REALIZADA POR MICROSCOPIA ELETRôNICA DE VARREDURA (MEV), ENQUANTO A COMPOSIçãO QUíMICA DO FILME SUPERFICIAL FOI AVALIADA POR ESPECTROSCOPIA DE ENERGIA DISPERSIVA DE RAIOS-X (EDS), COM O OBJETIVO DE VERIFICAR A PRESENçA DE INIBIDOR NA SUPERFíCIE DO AçO. OS RESULTADOS OBTIDOS DEMONSTRARAM QUE O [BMIM]BF4 ATUA COMO UM INIBIDOR DO TIPO MISTO COM EFEITO PREDOMINANTE NAS REAçõES ANóDICAS. UMA ADIçãO DE 2,5% DO INIBIDOR à SOLUçãO CORROSIVA EM TEMPERATURA AMBIENTE FOI CAPAZ DE REDUZIR A CORROSãO DA JUNTA SOLDADA DE AçO INOXIDáVEL DUPLEX EM 40,74%. A ANáLISE DA MORFOLOGIA DA SUPERFíCIE REVELOU UMA REDUçãO DOS DANOS SUPERFICIAIS NA PRESENçA DO INIBIDOR, SUGERINDO A FORMAçãO DE UM FILME PROTETOR PROPORCIONADO PELO LíQUIDO IôNICO. DESSA FORMA, CONCLUIU-SE QUE O TETRAFLUOROBORATO DE 1-BUTIL-3-METILIMIDAZóLIO APRESENTA POTENCIAL COMO UMA ALTERNATIVA SUSTENTáVEL PARA PROTEçãO CONTRA A CORROSãO EM AMBIENTES áCIDOS, PROMOVENDO A PRESERVAçãO DA INTEGRIDADE DO MATERIAL E A REDUçãO DE CUSTOS ASSOCIADOS à CORROSãO.

THE INFLUENCE OF THE 1-BUTYL-3-METHYLIMIDAZOLIUM TETRAFLUOROBORATE ([BMIM]BF4) IONIC LIQUID ON THE CORROSION INHIBITION OF THE WELDED AND HEAT-TREATED JOINT OF UNS S31803 DUPLEX STAINLESS STEEL IN A 1M SULFURIC ACID SOLUTION WAS INVESTIGATED BY ELECTROCHEMICAL TECHNIQUES. SURFACE MORPHOLOGY ANALYSIS WAS PERFORMED BY SCANNING ELECTRON MICROSCOPY (SEM), WHILE THE CHEMICAL COMPOSITION OF THE SURFACE FILM WAS EVALUATED BY ENERGY DISPERSIVE X-RAY SPECTROSCOPY (EDS), IN ORDER TO VERIFY THE PRESENCE OF THE INHIBITOR ON THE STEEL SURFACE. THE OBTAINED RESULTS DEMONSTRATED THAT [BMIM]BF4 ACTS AS A MIXED-TYPE INHIBITOR WITH A PREDOMINANT EFFECT ON ANODIC REACTIONS. ADDITION OF 2.5% INHIBITOR TO THE CORROSIVE SOLUTION AT ROOM TEMPERATURE WAS ABLE TO REDUCE CORROSION OF DUPLEX STAINLESS STEEL WELDED JOINT BY 45.6%. SURFACE MORPHOLOGY ANALYSIS REVEALED A REDUCTION IN SURFACE DAMAGE IN THE PRESENCE OF THE INHIBITOR, SUGGESTING THE FORMATION OF A PROTECTIVE FILM PROVIDED BY THE IONIC LIQUID. THUS, IT WAS CONCLUDED THAT 1-BUTYL-3-METHYLIMIDAZOLIUM TETRAFLUOROBORATE SHOWS POTENTIAL AS A SUSTAINABLE ALTERNATIVE FOR CORROSION PROTECTION IN ACIDIC ENVIRONMENTS, PROMOTING MATERIAL INTEGRITY PRESERVATION AND REDUCING COSTS ASSOCIATED WITH CORROSION.