Title

AVALIAÇÃO DA HOMOGENEIDADE MICROESTRUTURAL EM AÇOS COM ALTO ALUMÍNIO E DISTINTAS ADIÇÕES DE CARBONO E NIÓBIO FORJADO A QUENTE

EVALUATION OF MICROSTRUCTURAL HOMOGENEITY IN HOT FORGED HIGH ALUMINUM STEELS WITH DIFFERENT ADDITIONS OF CARBON AND NIOBIUM

Authorship

Gurgel, Mônica Aline Magalhães; Cruz, Renato Batista da; Botelho, Ramón Alves; Baêta Júnior, Eustáquio de Souza; Araújo, Leonardo Sales; Brandão, Luiz Paulo Mendonça; Paula, Andersan dos Santos

Gurgel, Mônica Aline Magalhães

I am this author

Cruz, Renato Batista da

I am this author

Botelho, Ramón Alves

I am this author

Baêta Júnior, Eustáquio de Souza

I am this author

Araújo, Leonardo Sales

I am this author

Brandão, Luiz Paulo Mendonça

I am this author

Paula, Andersan dos Santos

I am this author

DOI

10.5151/1516-392X-31987

Downloads

Abstract

Os aços passíveis de efeito TRIP (Transformation Induced Plasticity) denominados de aços TRIP surgiram durante o desenvolvimento de aços com a finalidade de satisfazer as exigências da indústria automotiva, devido a seu mecanismo particular de deformação. Este trabalho avalia amostras de aços na condição forjada, em escala laboratorial, de distintas composições químicas com alto teor de alumínio e distintas adições de carbono e nióbio visando a produção de uma liga susceptível ao efeito TRIP, via microscopia óptica e análises de difração de raios X (DRX), a fim de verificar a homogeneidade e as fases presentes na microestrutura. Por meio das análises obteve resultados satisfatórios para as condições de alto e baixo carbono com adição de nióbio (A1 e B1).

TRIP (Transformation Induced Plasticity) steels known as TRIP steels arose during the development of steels in order to meet the requirements of the automotive industry due to their particular deformation mechanism. This work evaluates steels samples hot forged in condition laboratory of different chemical compositions with high aluminum content and different additions of carbon and niobium aiming the production of an alloy susceptible to the TRIP effect, via optical microscopy and X-Ray diffraction (XRD) analysis in order to verify the homogeneity and the phases present in the microstructure. By means of the analyzes, it obtained satisfactory results for high and low carbon conditions with addition of niobium (A1 and B1).

Keywords

Aços TRIP; Caracterização microestrutural; DRX.

Steel TRIP; Microstructural characterization;XRD.