AVALIAÇÃO DA LIMPEZA SUPERFICIAL DA TIRA DE AÇO APÓS A SEÇÃO DE LIMPEZA DA CGL PELO TESTE DE REFLECTÂNCIA E ANÁLISE QUÍMICA DE ELEMENTOS RESIDUAIS

EVALUATION OF SURFACE CLEANLINESS OF STEEL STRIP AFTER THE CGL'S CLEANING SECTION BY THE REFLECTANCE TEST AND CHEMICAL ANALYZIS OF RESIDUAL ELEMENTS

Authorship

Guimaraes, Juliana Porto

Guimaraes, Juliana Porto

I am this author

DOI

10.5151/2594-5297-34889

Downloads

Abstract

A LIMPEZA DA SUPERFíCIE DA TIRA DE AçO NãO REVESTIDA APóS A SEçãO DE LIMPEZA é EXTREMAMENTE IMPORTANTE PARA EVITAR RESíDUOS E INCRUSTAçõES NOS ROLOS DA LINHA DE GALVANIZAçãO A QUENTE (CGL), A FALTA DE ADERêNCIA DO REVESTIMENTO à SUPERFíCIE DO SUBSTRATO E A CONTAMINAçãO DO BANHO DE ZN, PRINCIPALMENTE COM FE. O MéTODO TíPICO PARA AVALIAR A LIMPEZA DA SUPERFíCIE é O TESTE DE REFLETâNCIA, POIS é DE BAIXO CUSTO, REQUER POUCOS RECURSOS LABORATORIAIS, é NãO DESTRUTIVO E RáPIDO. CONSISTE NA APLICAçãO DE UMA FITA ADESIVA SENSíVEL à PRESSãO SOBRE A TIRA PARA COLETAR OS CONTAMINANTES E, POSTERIORMENTE, SUA AVALIAçãO POR UM REFLETôMETRO. NO ENTANTO, ESTA é UMA ANáLISE QUALITATIVA, E SEU RESULTADO é APENAS INDICATIVO. PORTANTO, NESTE ESTUDO FOI REALIZADA UMA ANáLISE COMPARATIVA ENTRE ESTE MéTODO E AS CONCENTRAçõES REMANESCENTES DE C E FE NAS SUPERFíCIES DE AçOS PROCESSADOS NA SEçãO DE LIMPEZA DA CGL2 DA UNIGAL. FORAM OBTIDAS CORRELAçõES ESTATISTICAMENTE SIGNIFICATIVAS ENTRE AS MEDIDAS DE REFLETâNCIA E AS CONCENTRAçõES REMANESCENTES DE C, MEDIDAS POR ANALISADOR DE C, E FE, ANALISADAS POR ESPECTROMETRIA DE EMISSãO óTICA COM PLASMA INDUTIVAMENTE ACOPLADO. ASSIM, FOI POSSíVEL VALIDAR O TESTE DE REFLETâNCIA FORNECENDO SUBSíDIOS PARA UM MELHOR ENTENDIMENTO DESTE PARâMETRO DE PROCESSO EXTREMAMENTE RELEVANTE PARA A QUALIDADE SUPERFICIAL E ADERêNCIA DO REVESTIMENTO DE AçOS GALVANIZADOS A QUENTE.

THE SURFACE CLEANLINESS OF THE UNCOATED STEEL STRIP AFTER THE CLEANING SECTION IS EXTREMELY IMPORTANT TO AVOID RESIDUE AND INCRUSTATION ON THE HOT-DIP GALVANIZING LINE (CGL) ROLLS, THE LACK OF ADHESION OF THE COATING TO THE SUBSTRATE SURFACE AND CONTAMINATION OF THE ZN BATH, MAINLY WITH FE. THE TYPICAL METHOD TO ASSESS THE SURFACE CLEANLINESS IS THE REFLECTANCE TEST, AS IT IS LOW COST, REQUIRES FEW LABORATORY RESOURCES, IS NON-DESTRUCTIVE AND FAST. IT CONSISTS OF APPLYING A PRESSURE-SENSITIVE ADHESIVE TAPE OVER THE STRIP TO COLLECT THE CONTAMINANTS AND, LATER, THEIR EVALUATION BY A REFLECTOMETER. HOWEVER, THIS IS A QUALITATIVE ANALYSIS, AND ITS RESULT IS ONLY INDICATIVE. THEREFORE, IN THIS STUDY A COMPARATIVE ANALYSIS WAS PERFORMED BETWEEN THIS METHOD AND THE C AND FE REMAINED CONCENTRATIONS THE STEELS’ SURFACES PROCESSED IN THE CLEANING SECTION OF CGL2 OF UNIGAL. STATISTICALLY SIGNIFICANT CORRELATIONS WERE OBTAINED BETWEEN THE REFLECTANCE MEASUREMENTS AND THE REMAINED CONCENTRATIONS OF C, MEASURED BY C ANALYZER, AND FE, ANALYZED BY INDUCTIVELY COUPLED PLASMA OPTICAL EMISSION SPECTROMETRY. THUS, IT WAS POSSIBLE TO VALIDATE THE REFLECTANCE TEST PROVIDING SUBSIDIES FOR A BETTER UNDERSTANDING OF THIS EXTREMELY RELEVANT PROCESS PARAMETER FOR THE SURFACE QUALITY AND COATING ADHESION OF HOT-DIP GALVANIZED STEELS

Keywords

Limpeza eletrolítica; Teste de refletância; Galvanização a quente

Electrolytic cleaning; Reflectance test; Hot-dip galvanizing