Title

AVALIAÇÃO DA MICROESTRUTURA DE ARGILA CAOLINÍTICA EM FUNÇÃO DA TEMPERATURA DE QUEIMA

EVALUATION OF MICROSTRUCTURE IN KAOLINITIC CLAY AS A FUNCTION OF FIRING TEMPERATURE

Authorship

VIEIRA, CARLOS MAURÍCIO FONTES; DELAQUA, GEOVANA CARLA GIRONDI

VIEIRA, CARLOS MAURÍCIO FONTES

I am this author

DELAQUA, GEOVANA CARLA GIRONDI

I am this author

DOI

10.5151/2594-5327-41271

Downloads

Abstract

FOI AVALIADA A MICROESTRUTURA DE UMA ARGILA CAULINíTICA UTILIZADA EM CERâMICA VERMELHA DO MUNICíPIO DE CAMPOS DOS GOYTACAZES, ESTADO DO RIO DE JANEIRO, BRASIL. AS TRANSFORMAçõES DE QUEIMA FORAM ESTUDADAS POR DIFRAçãO DE RAIOS X, ANáLISE TéRMICA (DTA/TGA/DTG) E MICROSCOPIA ELETRôNICA DE VARREDURA. AS PROPRIEDADES FíSICAS COMO RETRAçãO LINEAR E ABSORçãO DE áGUA TAMBéM FORAM AVALIADAS EM AMOSTRAS PRENSADAS QUE FORAM QUEIMADAS EM TEMPERATURAS VARIANDO DE 900 A 1100ºC. OS RESULTADOS INDICARAM QUE A ARGILA APRESENTA COMPORTAMENTO REFRATáRIO DURANTE A QUEIMA DEVIDO AO PREDOMíNIO DA CAULINITA, ELEVADA PERDA DE MASSA E PRESENçA DE HIDRóXIDOS. EM ALTAS TEMPERATURAS A MICROESTRUTURA DA ARGILA SOFRE TRANSFORMAçõES IMPORTANTES, COMO DIMINUIçãO ACENTUADA DA POROSIDADE E ALTERAçõES NAS FASES CRISTALINAS. FORMARAM-SE HEMATITA, ESPINéLIO SI-AL, MULITA E PLAGIOCLáSIO E MICA E QUARTZO, FASES RESIDUAIS, FORAM PARCIALMENTE DISSOLVIDOS NA FASE LíQUIDA

THE MICROSTRUCTURE OF A KAOLINITIC CLAY USED IN RED CERAMIC FROM THE COUNTY OF CAMPOS DOS GOYTACAZES, STATE OF RIO DE JANEIRO, BRAZIL WAS EVALUATED. THE FIRING TRANSFORMATIONS WERE STUDIED BY X-RAY DIFFRACTION, THERMAL ANALYSIS (DTA/TGA/DTG), AND SCANNING ELECTRON MICROSCOPY. PHYSICAL PROPERTIES SUCH AS LINEAR SHRINKAGE AND WATER ABSORPTION WERE ALSO EVALUATED IN PRESSED SAMPLES FIRED AT TEMPERATURES VARYING FROM 900 TO 1100ºC. THE RESULTS INDICATED THAT THE CLAY PRESENTS A REFRACTORY BEHAVIOR DURING FIRING DUE TO THE KAOLINITE PREDOMINANCE, ELEVATED WEIGHT LOSS AND THE PRESENCE OF HYDROXIDES. AT HIGH TEMPERATURES THE MICROSTRUCTURE OF THE CLAY SUFFERS IMPORTANT TRANSFORMATIONS, SUCH AS A MARKED DECREASE ON THE POROSITY AND CHANGES ON THE CRYSTALLINE PHASES. HEMATITE, SI-AL SPINEL, MULLITE AND PLAGIOCLASE WERE FORMED AND MICA AND QUARTZ, RESIDUAL PHASES, WERE PARTIALLY DISSOLVED IN THE LIQUID PHASE

Keywords

Argila, kaolinita, microstructura, Queima

Clay, KAOLINITE, Microstructure, firing.