Title

AVALIAÇÃO DA RESISTÊNCIA EM TRAÇÃO DE COMPÓSITOS DE MATRIZ EPÓXI REFORÇADA COM RESÍDUO DE FIBRAS DE POLIÉSTER

EVALUATION OF THE TENSILE STRENGTH OF EPOXY MATRIX COMPOSITES REINFORCED WITH RESIDUE POLYESTER FIBERS

DOI

10.5151/2594-5327-41393

Downloads

Abstract

O USO CONSCIENTE DE RECURSOS E A DESTINAçãO ADEQUADA DE RESíDUOS SóLIDOS é UMA PREOCUPAçãO CRESCENTE PARA A SOCIEDADE. O USO CONSCIENTE DE RECURSOS AJUDA A PRESERVAR MATéRIAS-PRIMAS GARANTINDO SUA DISPONIBILIDADE FUTURA E A GESTãO ADEQUADA DE RESíDUOS SóLIDOS REDUZ A POLUIçãO DO SOLO, DA áGUA E DO AR, MITIGANDO OS EFEITOS NEGATIVOS SOBRE A SAúDE HUMANA E O MEIO AMBIENTE. NA ENGENHARIA DE MATERIAIS, SãO INúMERAS PESQUISAS QUE BUSCAM DAR DESTINO E UTILIZAçãO PARA RESíDUOS COM APLICAçõES VIáVEIS. O RESíDUO UTILIZADO NA FABRICAçãO DOS COMPóSITOS ANALISADOS NESTE TRABALHO é PROVENIENTE DE EMPRESAS DE RECAPAGEM DE PNEUS E SãO TECIDOS DE POLIéSTER COM BORRACHA REMANESCENTE. FORAM FABRICADOS COMPóSITOS COM VOLUME DE INCLUSãO DE RESíDUO VARIANDO ENTRE 0, 5, 10 E 15%, ONDE APóS A ANáLISE DOS RESULTADOS DO ENSAIO DE TRAçãO, EM CONFORMIDADE COM NORMA ASTM D638, MOSTROU-SE O AUMENTO DA RESISTêNCIA à TRAçãO EM 20,6% EM RELAçãO A MATRIZ SEM REFORçO, ALCANçANDO 56,73 (±5,51) MPA NESTA PROPRIEDADE MECâNICA PARA COMPOSIçãO COM 15% DE RESíDUO. OS VALORES DAS PROPRIEDADES OBTIDAS NO ENSAIO DE TRAçãO FORAM COMPARADOS ESTATISTICAMENTE PELOS TESTES ANOVA E TUKEY, ESTES QUE MOSTRARAM QUE A INCLUSãO DAS FIBRAS RESIDUAIS DE POLIéSTER NA MATRIZ EPóXI TROUXE UM AUMENTO SIGNIFICATIVO DA RESISTêNCIA A TRAçãO E DEFORMAçãO TOTAL PARA O COMPóSITO COM INCORPORAçãO DE 15% EM VOLUME DE FIBRA. ESSES RESULTADOS APONTAM PARA A UTILIZAçãO DESTE RESíDUO COMO REFORçO NA FABRICAçãO DE COMPóSITOS UTILIZANDO EPóXI COMO MATRIZ.

 

THE CONSCIOUS USE OF RESOURCES AND THE APPROPRIATE DISPOSAL OF SOLID WASTE IS A GROWING CONCERN FOR SOCIETY. THE CONSCIOUS USE OF RESOURCES HELPS PRESERVE RAW MATERIALS, GUARANTEEING THEIR FUTURE AVAILABILITY, AND THE APPROPRIATE MANAGEMENT OF SOLID WASTE REDUCES SOIL, WATER AND AIR POLLUTION, MITIGATING NEGATIVE EFFECTS ON HUMAN HEALTH AND THE ENVIRONMENT. IN MATERIALS ENGINEERING, THERE IS COUNTLESS RESEARCH THAT SEEKS TO FIND A DESTINATION AND USE FOR WASTE WITH VIABLE APPLICATIONS. THE WASTE USED IN THE MANUFACTURE OF THE COMPOSITES ANALYZED IN THIS WORK COMES FROM TIRE RETREADING COMPANIES AND IS POLYESTER FABRICS WITH REMAINING RUBBER. COMPOSITES WERE MANUFACTURED WITH RESIDUE INCLUSION VOLUME VARYING BETWEEN 0, 5, 10 AND 15%, WHERE AFTER ANALYZING THE RESULTS OF THE TENSILE TEST, IN ACCORDANCE WITH THE ASTM D638 STANDARD, AN INCREASE IN TENSILE STRENGTH WAS SHOWN BY 20. 6% IN RELATION TO THE MATRIX WITHOUT REINFORCEMENT, REACHING 56.73 (±5.51) MPA IN THIS MECHANICAL PROPERTY FOR A COMPOSITION WITH 15% RESIDUE. THE VALUES OF THE PROPERTIES OBTAINED IN THE TENSILE TEST WERE STATISTICALLY COMPARED USING THE ANOVA AND TUKEY TESTS, WHICH SHOWED THAT THE INCLUSION OF RESIDUAL POLYESTER FIBERS IN THE EPOXY MATRIX BROUGHT A SIGNIFICANT INCREASE IN TENSILE STRENGTH AND TOTAL DEFORMATION FOR THE COMPOSITE WITH INCORPORATION OF 15 % FIBER VOLUME. THESE RESULTS POINT TO THE USE OF THIS RESIDUE AS REINFORCEMENT IN THE MANUFACTURE OF COMPOSITES USING EPOXY AS A MATRIX.

Keywords

Materiais compósitos; Fibra de Poliéster; Resíduo; Resistência à Tração

Composite materials; Polyester Fiber; Residue; Tensile Strength.

How to refer

NETO, LEONCIO SOARES GALVÃO; PINHEIRO, MIRIANE ALEXANDRINO; SILVA, ALISSON CLAY RIOS DA; CANDIDO, VERÔNICA SCARPINI. AVALIAÇÃO DA RESISTÊNCIA EM TRAÇÃO DE COMPÓSITOS DE MATRIZ EPÓXI REFORÇADA COM RESÍDUO DE FIBRAS DE POLIÉSTER , p. 3221-3228. In: 77º Congresso Anual da ABM - Internacional, São Paulo, Brasil, 2024.