AVALIAÇÃO DA SOLDABILIDADE GMAW DO AÇO TRIP1000 ELETROGALVANIZADO

ASSESSMENT OF GMAW WELDABILITY OF ELECTROGALVANIZED TRIP1000 STEEL

Authorship

BORBA, TADEU MESSIAS DONIZETE; SILVA, RODOLFO JÚNIOR CONCEIÇÃO; TOLEDO, EUGÊNIO DE CARVALHO; MIRANDA, VICTOR HORTA; SOARES, LEANDRO MATOS LOPES

BORBA, TADEU MESSIAS DONIZETE

I am this author

SILVA, RODOLFO JÚNIOR CONCEIÇÃO

I am this author

TOLEDO, EUGÊNIO DE CARVALHO

I am this author

MIRANDA, VICTOR HORTA

I am this author

SOARES, LEANDRO MATOS LOPES

I am this author

DOI

10.5151/2594-5327-40587

Downloads

Abstract

A USIMINAS TEM DIRECIONADO ESFORçOS PARA O DESENVOLVIMENTO DE AçOS AVANçADOS DE ALTA RESISTêNCIA, VISANDO ATENDER àS DEMANDAS DO SETOR AUTOMOTIVO. DENTRE ESSES MATERIAIS, DESTACA-SE O AçO TRIP (TRANSFORMATION INDUCED PLASTICITY) ELETROGALVANIZADO (EG) DA CLASSE DE 1000 MPA DE RESISTêNCIA (TRIP1000EG). NESSE TRABALHO, FOI AVALIADA A SOLDABILIDADE A ARCO COM PROTEçãO GASOSA (GMAW - GAS METAL ARC WELDING) ROBOTIZADA DO AçO TRIP1000EG DE 1,50 MM DE ESPESSURA. FORAM OBTIDAS JUNTAS ISENTAS DE DESCONTINUIDADES E COM CORDõES GEOMETRICAMENTE ADEQUADOS AOS CRITéRIOS DA NORMA SEP1220. ALéM DISSO, ENSAIOS RADIOGRáFICOS REVELARAM QUE OS CORDõES DE SOLDA APRESENTARAM BAIXA DENSIDADE DE POROS, INFERIOR A 2,5%, INDICANDO QUE O CONSUMíVEL UTILIZADO é APROPRIADO PARA A SOLDAGEM DO AçO COMO ELETROGALVANIZADO. OS RESULTADOS CONFIRMARAM QUE OS PARâMETROS GMAW ELABORADOS PARA ATENDER AOS CRITéRIOS DE QUALIDADE DA NORMA FORAM ADEQUADOS PARA A SOLDAGEM DO AçO E PODEM SER UTILIZADOS COMO REFERêNCIA PARA O DESENVOLVIMENTO DA ENGENHARIA DE APLICAçãO DESSE MATERIAL NA INDúSTRIA AUTOMOTIVA.

USIMINAS HAS DIRECTED EFFORTS TOWARDS THE DEVELOPMENT OF AHSS - ADVANCED HIGH-STRENGTH STEELS, AIMING TO MEET THE DEMANDS OF THE AUTOMOTIVE SECTOR. AMONG THESE MATERIALS, ELECTROGALVANIZED (EG) TRIP STEEL OF THE 1000 MPA CLASS (TRIP1000EG) STANDS OUT. IN THIS WORK, THE ROBOTIC GAS METAL ARC WELDING (GMAW) OF A TRIP1000EG STEEL, WITH 1.50 MM THICKNESS, WAS EVALUATED. WELD JOINTS WITHOUT DISCONTINUITIES WERE OBTAINED, WITH BEADS GEOMETRICALLY APPROPRIATE TO THE CRITERIA OF THE SEP1220 STANDARD. FURTHERMORE, THROUGH RADIOGRAPHIC TESTS, IT WAS IDENTIFIED THAT THE WELD BEADS HAD A LOW PORE DENSITY, LESS THAN 2.5%, INDICATING THAT THE CONSUMABLE USED WAS ADEQUATE FOR WELDING EG STEELS. THE RESULTS OF THIS STUDY CONFIRM THAT THE GMAW PARAMETERS OBTAINED WERE SUITABLE FOR WELDING STEEL AND CAN BE USED AS A REFERENCE FOR THE DEVELOPMENT OF APPLICATION ENGINEERING OF THIS MATERIAL IN THE AUTOMOTIVE INDUSTRY.

Keywords

Aço TRIP1000EG; Soldabilidade; Processo GMAW

TRIP1000EG Steel; Weldability; GMAW Process.