AVALIAÇÃO DAS PROPRIEDADES MECÂNICAS DE COMPÓSITOS PRODUZIDOS COM RESÍDUOS DA INDUSTRIA MOVELEIRA

MECHANICAL PROPERTIES EVALUATION OF COMPOUNDS PRODUCED WITH WASTE OF THE MOBILE INDUSTRY

DOI

10.5151/2594-5327-33325

Downloads

Abstract

A indústria de móveis gera cerca de 19.255.000 m³/ano de resíduos de madeira com potencial para reciclagem de materiais. Este projeto tem com o objetivo minimizar a destinação final de resíduos de Medium Density Fiberboard (MDF) através do desenvolvimento de um novo laminado de MDF reprocessado. Para tanto fez-se a coleta de MDF cru produzidos por corte a laser, em seguida o material foi triturado em moinho de facas e quarteado. O resíduo de MDF triturado foi misturado com resina poliéster nas proporções de 1 para 3 de resina poliéster em peso. A partir da formulação foi feito um laminado de 3 a 4 mm de espessura, onde também foi desenvolvido corpos de prova para a realização de ensaios mecânicos, tais como ensaio de tração, flexão e impacto, para determinação das propriedades do novo laminado. Os resultados esperados são a identificação das proporções ideais entre resina e MDF triturado e a resistência a impacto, tração e flexão determinadas pelos ensaios mecânicos

 

The furniture industry generates about 19,255,000 m³ / year of wood waste with potential for recycling of materials. This project aims to minimize the final destination of Medium Density Fiberboard (MDF) waste through the development of a reprocessed MDF laminate. In order to do so, the raw MDF was produced by laser cutting, then the material was ground in a knife mill and quartet. The crushed MDF residue was blended with polyester resin in the proportions of 1 to 3 polyester resin by weight. From the formulation a laminate of 3 to 4 mm thickness was made, where also test specimens were developed to perform mechanical tests, such as tensile, flexural and impact tests, to determine the properties of the new laminate. The expected results are the identification of the ideal proportions between resin and crushed MDF and the impact, tensile and flexural strength determined by the mechanical tests

Keywords

Resíduos de Madeira; Reciclagem; Ensaios Mecânicos

Waste Wood; Recycling; Mechanical Tests