AVALIAÇÃO DE CORPOS MOEDORES DE FERRO FUNDIDO BRANCO ALTO CROMO UTILIZADOS NA MOAGEM DA PELOTIZAÇÃO

EVALUATION OF HIGH CHROMIUM WHITE CAST IRON GRINDING BODIES USED IN MILLING OF THE PELLETIZING

DOI

10.5151/2594-357X-40330

Downloads

Abstract

O consumo de corpos moedores é um dos principais itens de custo no processamento de minérios, tornando a etapa de moagem dispendiosa para a pelotização. O presente estudo foi desenvolvido para avaliar cinco tipos de corpos moedores constituídos de ferro fundido branco alto cromo (FFBAC) com diferentes composições químicas e tratamentos térmicos. As amostras foram caracterizadas física, química e metalograficamente, utilizando as técnicas de análise de dureza Rockwell C (HRC), espectrometria de emissão óptica (OES), micro e macrografia óptica e análise dimensional. Para análise do desgaste, foi aplicado o teste de bolas marcadas (MBT) realizado com duas coletas de amostras, totalizando 1.258 h de operação do moinho. Concluiu-se que a liga 2H135 (34%p Cr) apresentou taxa de desgaste de 1,82 µm/h, indicando redução de 18% de desgaste quando comparado com a referência e potencial redução de custos na moagem com aplicação deste material como corpo moedor.

 

Grinding media consumption is one of the main cost items in ore processing, making the grinding step expensive for pelletizing. The present study was developed to evaluate five grinding media types consisting of high chromium white cast iron with different chemical compositions and heat treatments. The samples were characterized physically, chemically and metallographically, using Rockwell C hardness (HRC) analysis techniques, optical emission spectrometry (OES), optical micro and macrography and dimensional analysis. For wear analysis, the marked balls test (MBT) was applied. The MBT was performed with two sample collections, totaling 1,258 h of mill operation. It was concluded that the alloy 2H135 (34%p Cr) presented wear rate of 1.82 μm/h, indicating a reduction of 18% wear when compared to the reference and potential cost reduction in grinding with application of this material.

Keywords

Moagem; Corpos moedores; Ferro fundido branco alto cromo; Desgaste.

Grinding; Grinding balls; High chromium white cast iron; Wear.