Title

AVALIAÇÃO DE DESEMPENHO DE FERRAMENTAS DE AÇO AISI 1045 REVESTIDAS COM FILME DE TIN PARA PROCESSO DE SOLDAGEM POR ATRITO (FSW)

PERFORMANCE EVALUATION OF AISI 1045 STEEL TOOLS COATED WITH TIN FILM FOR FRICTION WELDING PROCESS (FSW)

Authorship

OLIVEIRA, PAULO RODRIGUES; NEVES, HENRIQUE HOCHLEITNER; SILVA, ALEXANDRE MELLO DE PAULO; CAMPOS, JOSÉ BRANT DE; LETÍCIA DOS SANTOS AGUILERA; TEODORO, BRUNO NEVES TARGINO; SILVEIRA, JOSÉ LUÍS LOPES DA

OLIVEIRA, PAULO RODRIGUES

I am this author

NEVES, HENRIQUE HOCHLEITNER

I am this author

SILVA, ALEXANDRE MELLO DE PAULO

I am this author

CAMPOS, JOSÉ BRANT DE

I am this author

LETÍCIA DOS SANTOS AGUILERA

24 Articles, 4327 downloads

TEODORO, BRUNO NEVES TARGINO

I am this author

SILVEIRA, JOSÉ LUÍS LOPES DA

I am this author

DOI

10.5151/2594-5327-34751

Downloads

Abstract

A NECESSIDADE DE SE REALIZAR SOLDAS COM DEMANDAS CADA VEZ MAIS ESPECÍFICAS, COMO A UNIÃO ENTRE MATERIAIS DISSIMILARES E DEVIDO AO ALTO CUSTO QUE OCORRE NA REALIZAÇÃO DE SOLDAS EM LIGAS QUE TRADICIONALMENTE APRESENTAM DIFICULDADE DE UNIÃO PELOS PROCESSOS DE SOLDAGENS CONVENCIONAIS, SÃO DIFICULDADES IMPOSTAS NO RAMO DA SOLDAGEM. NESTE CENÁRIO, SURGE O PROCESSO DE SOLDAGEM POR FRICÇÃO DENOMINADO DE FRICTION STIR WELDING (FSW), QUE SE DESTACA DOS OUTROS PROCESSOS COMUNS DE SOLDAGEM, JUSTAMENTE POR SER CAPAZ DE RESPONDER A ESSAS SOLICITAÇÕES DE MANEIRA EFICIENTE. O OBJETIVO DESTE TRABALHO FOI AVALIAR A QUALIDADE DE UM FILME DE TIN DEPOSITADO POR MAGNETRON SPUTTERING EM FERRAMENTAS DE AÇO AISI 1045 PARA O PROCESSO FSW VISANDO O AUMENTO DA SUA VIDA ÚTIL. O FILME FOI CARACTERIZADO POR MICROSCOPIA ELETRÔNICA DE VARREDURA (MEV) E ESPECTROSCOPIA DE ENERGIA DISPERSIVA (EDS) QUANTO A MORFOLOGIA, HOMOGENEIDADE DA DEPOSIÇÃO E INTEGRIDADE APÓS ENSAIOS DE FRICTION STIR PROCESS (FSP). O DESEMPENHO DAS FERRAMENTAS FOI AVALIADO PELO ENSAIO FSP, COMPARANDO ESFORÇOS RESULTANTES E DEFORMAÇÕES ENTRE AS FERRAMENTAS COM E SEM O FILME.

THE NEED TO CARRY OUT WELDS WITH INCREASINGLY SPECIFIC DEMANDS, SUCH AS THE UNION BETWEEN DISSIMILAR MATERIALS AND DUE TO THE HIGH COST, THAT OCCURS IN PERFORMING WELDS IN ALLOYS THAT TRADITIONALLY HAVE DIFFICULTY IN JOINING BY CONVENTIONAL WELDING PROCESSES, ARE DIFFICULTIES IMPOSED IN THE FIELD OF WELDING. IN THIS SCENARIO, THE FRICTION WELDING PROCESS KNOWN AS FRICTION STIR WELDING (FSW) EMERGES, WHICH STANDS OUT FROM OTHER COMMON WELDING PROCESSES, PRECISELY BECAUSE IT IS ABLE TO RESPOND TO THESE REQUESTS EFFICIENTLY. THE OBJECTIVE OF THIS WORK WAS TO EVALUATE THE QUALITY OF A TIN FILM DEPOSITED BY MAGNETRON SPUTTERING ON AISI 1045 STEEL TOOLS FOR THE FSW PROCESS, AIMING TO INCREASE ITS USEFUL LIFE. THE FILM WAS CHARACTERIZED BY SCANNING ELECTRON MICROSCOPY (SEM) AND ENERGY DISPERSION SPECTROSCOPY (EDS) FOR MORPHOLOGY, DEPOSITION HOMOGENEITY AND INTEGRITY AFTER FRICTION STIR PROCESS (FSP) TESTS. THE PERFORMANCE OF THE TOOLS WAS EVALUATED BY THE FSP TEST, COMPARING RESULTING EFFORTS AND DEFORMATIONS BETWEEN THE TOOLS WITH AND WITHOUT THE FILM.

Keywords

Magnetron Sputtering; Microscopia Eletrônica de Varredura; Friction Stir Process; Filme de TiN.

Magnetron Sputtering; Scanning Electron Microscopy; Friction Stir Process; TiN film.