Title

AVALIAÇÃO DE PARÂMETROS DE PROCESSO NA QUALIDADE FINAL DE UMA JUNTA DE ALUMÍNIO (2024- T351) SOLDADA POR FSW – FRICTION STIR WELDING

WELDING PARAMETER EVALUATION ON THE QUALITY OF A 2024-T351 ALUMINUM ALLOY WELDED BY FRICTION STIR WELDING - FSW

Authorship

Potomati, Fernanda; Carletti, Camilo Bento; Epiphanio, Ivan Dalla Valle; Kuri, Marcelo Pavan; Alcântara, Nelson Guedes de; Santos, Jorge Fernandez dos

Potomati, Fernanda

I am this author

Carletti, Camilo Bento

I am this author

Epiphanio, Ivan Dalla Valle

I am this author

Kuri, Marcelo Pavan

I am this author

Alcântara, Nelson Guedes de

I am this author

Santos, Jorge Fernandez dos

I am this author

DOI

10.5151/2594-5327-0288

Downloads

Abstract

Este trabalho tem como objetivo avaliar o efeito de diferentes parâmetros do processo de soldagem FSW - Friction Stir Welding em uma liga Al2024-T351, de forma a correlacioná-los com as medidas de ciclos térmicos, microestrutura (via microscopia eletrônica de varredura), e propriedades mecânicas (ensaio de tração e microdureza). Os resultados de tração e microdureza mostraram que as soldas produzidas com maior velocidade de soldagem (soldas frias) apresentam resistência mecânica mais próxima a do metal de base, do que as soldas produzidas com baixa velocidade de soldagem (quentes). Com relação à análise microestrutural, as soldas quentes apresentaram um maior efeito do aporte térmico pela ação de superenvelhecimento de precipitados.

The objective of this work was to evaluate the effects of FSW – Friction Stir Welding process parameters on a 2024-T351 aluminum alloy, by performing welds with different parameters and correlate them with thermal cycles measurements, final microstructure (through scanning electron microscopy), and mechanical properties (tensile and microhardness testing). Tensile and microhardness results showed that the welds performed with higher weld speed (cold welds) had mechanical resistance more similar to the base material as the others (medium and hot welds). The microstructural analysis demonstrated that the hot welds suffered greater influence of the thermal cycles than the colder welds since they presented an advanced over ageing process.

Keywords

Friction stir welding; Ciclos térmicos; Alumínio; Propriedades mecânicas.

Friction stir welding; Thermal analysis; Aluminum; Mechanical properties.