Title

AVALIAÇÃO DE PROPRIEDADES MECÂNICAS E MICROESTRUTURAIS DE JUNTAS DE AÇOS MARAGING SOLDADAS POR MEIO DOS PROCESSOS LASER E FEIXE DE ELÉTRONS

EVALUATION OF MECHANICAL AND MICROSTRUCTURAL PROPERTIES OF JOINTS IN MARAGING STEEL WELDED BY LASER AND ELECTRON BEAM WELDING

Authorship

Maximo, Henry Wilson Pohling; Rossi, Wagner de; Neves, Maurício David Martins das

Maximo, Henry Wilson Pohling

I am this author

Rossi, Wagner de

I am this author

Neves, Maurício David Martins das

I am this author

DOI

10.5151/2594-5327-22970

Downloads

Abstract

Neste trabalho estudaram-se diversas condições de soldagem com laser de Nd:YAG realizada em aço maraging 350 - ASTM A 538 Grade C e os resultados foram comparados com juntas soldadas com o processo feixe de elétrons. As soldagens realizadas com o processo por feixe de elétrons possuem um procedimento de soldagem qualificado. A junta selecionada para a elaboração do trabalho foi do tipo sobreposta com material de base de espessuras diferentes, respectivamente iguais a 1,00 mm e 0,78 mm. As juntas soldadas foram avaliadas por: ensaio de microdureza Vickers e caracterização microestrutural das diversas regiões das juntas soldadas. Os resultados indicam que as condições usadas em ambos os processos de soldagem foram satisfatórios e atingiram a profundidade de penetração mínima desejada.

In this work, it is intended to analyze the laser welding in maraging 350 steel ASTM A 538 Grade C and the results were compared with welded joints of electron beam welding. The welding process performed with electron beam welding has a qualified welding procedure. The joint chosen for the preparation of the work was the lap joint type with different thicknesses base material respectively equal to 1,00 mm and 0,78 mm. The welded joints were evaluated by mechanical tests like Vickers microhardness and microstructural characterization of the various regions of the welded joints. The results indicate that the conditions used for both welding process were satisfactory and reached the desired minimum penetration depth.

Keywords

Maraging 350; Soldagem com feixe laser; Soldagem com feixe de elétrons.

Maraging 350; Laser beam welding; Electron beam welding.