AVALIAÇÃO DO AMACIAMENTO DE UM AÇO ESTRUTURAL SAE 4340 UTILIZANDO ENSAIOS DE TORÇÃO A QUENTE

EVALUATION OF THE SOFTENING OF A STRUCTURAL STEEL SAE 4340 USING THE HOT TORSION TEST

Authorship

Marques, Armando; Souza, Rafael Agrizzi de; Tasca, Mario Roberto Bellini; Nogueira, Luciana; Machado, Marcelo Lucas Pereira

Marques, Armando

I am this author

Souza, Rafael Agrizzi de

I am this author

Tasca, Mario Roberto Bellini

I am this author

Nogueira, Luciana

I am this author

Machado, Marcelo Lucas Pereira

I am this author

DOI

10.5151/2594-5327-20911

Downloads

Abstract

Foram realizados ensaios de torção a quente com dupla deformação em um aço estrutural SAE 4340. A temperatura do ensaio e a taxa de deformação foram mantidas constantes em 1.050°C e 0,2 s-1 respectivamente, variou-se a deformação aplicada de (0,2 e 0,4) e o tempo entre passes (1 s, 5 s e 40 s). As amostras foram aquecidas até a temperatura de 1.200°C e mantidas nessa temperatura por 180 s (encharque) para completa homogeneização. A seguir foram resfriadas a uma taxa média 1ºC/s até a temperatura de deformação. A avaliação das características de amaciamento estático e metadinâmico do material foi feita a partir das curvas de escoamento plástico. Verificaram-se características similares de amaciamento nas duas deformações ensaiadas, com a fração amaciada crescendo com o tempo entre passes e com o aumento da deformação. Observou-se que houve refinamento dos grãos para o material que foi submetido a uma deformação de 0,4.

Tests were performed with double hot torsion deformation in structural steel SAE 4340. The test temperature and strain rate were kept constant at 1,050°C and 0.2 s-1 respectively, was varied to applied strain (0.2 and 0.4) and the time between passes (1 s, 40 s and 5 s). The samples were heated to a temperature of 1,200°C and maintained at this temperature for 180 seconds (soaking) to complete homogenization. The following were cooled at an average rate of 1°C/s until the temperature of deformation. Evaluation of the softening characteristics of the static and metadynamic material were made from plastic flow curves. There have similar softening characteristics on both strains tested, with the softened fraction increasing with time between passes and with increasing deformation. It was observed that there refinement of grain to material that has been subjected to a deformation of 0.4.

Keywords

Torção a quente; Fração de amaciamento; SAE 4340.

Hot torsion; Fraction of softening; SAE 4340.