AVALIAÇÃO DO EFEITO DA VARIAÇÃO EM PARÂMETROS EXPERIMENTAIS SOBRE A RESISTÊNCIA À CORROSÃO LOCALIZADA DO AÇO INOXIDÁVEL 316L

EVALUATION OF THE EFFECT OF VARIATIONS IN EXPERIMENTAL PARAMETERS ON THE RESISTANCE TO LOCALIZED CORROSION OF 316L STAINLESS STEEL

Authorship

COSTA, SAMUEL MOREIRA

COSTA, SAMUEL MOREIRA

I am this author

DOI

10.5151/2594-4711-40706

Downloads

Abstract

A CORROSãO é UM PROCESSO NATURAL DE DEGRADAçãO QUE ATINGE OS METAIS, ATRAVéS DE AçãO QUíMICA OU ELETROQUíMICA DO MEIO AMBIENTE. OS AçOS INOXIDáVEIS APRESENTAM ELEVADA RESISTêNCIA à CORROSãO EM UMA GRANDE DIVERSIDADE DE MEIOS. ISSO OCORRE PELA FORMAçãO DE UM FINO FILME DE óXIDO DE CROMO ESTáVEL SOB A SUPERFíCIE, QUE IMPEDE O CONTATO DE ESPéCIES AGRESSIVAS COM O SUBSTRATO METáLICO. O OBJETIVO DESTE ESTUDO FOI AVALIAR O EFEITO DA VARIAçãO EM PARâMETROS EXPERIMENTAIS NA RESISTêNCIA à CORROSãO LOCALIZADA DO AçO INOXIDáVEL AISI 316L. AMOSTRAS OBTIDAS A PARTIR DE UMA CHAPA DO AçO FORAM SUBMETIDAS A ANáLISE POR MICROSCOPIA ELETRôNICA DE VARREDURA, PARA CARACTERIZAçãO MICROESTRUTURAL. PARA CARACTERIZAçãO ELETROQUíMICA, FORAM REALIZADOS ENSAIOS DE POLARIZAçãO CíCLICA EM DIVERSAS CONDIçõES EXPERIMENTAIS, VARIANDO CONCENTRAçãO DE CLORETOS E DENSIDADE DE CORRENTE LIMITE DA VARREDURA. OS RESULTADOS EXPRESSAM A INFLUêNCIA DA AGRESSIVIDADE DOS íONS CLORETOS EM SOLUçãO E A IMPORTâNCIA DA CARGA GERADA DURANTE A CORROSãO POR PITES PARA O FENôMENO DA REPASSIVAçãO. ASSIM, O ESTUDO VERIFICA O EFEITO DESSAS VARIáVEIS EXPERIMENTAIS NA CORROSãO LOCALIZADA DO AçO INOXIDáVEL AISI 316L.

CORROSION IS A NATURAL DEGRADATION PROCESS THAT AFFECTS METALS THROUGH CHEMICAL OR ELECTROCHEMICAL ACTION OF THE ENVIRONMENT. STAINLESS STEELS ARE HIGHLY RESISTANT TO CORROSION IN A WIDE VARIETY OF CONDITIONS. THIS IS DUE TO THE FORMATION OF A THIN, STABLE CHROMIUM OXY-HYDROXIDE FILM ON THE SURFACE, WHICH PREVENTS AGGRESSIVE SPECIES FROM COMING INTO CONTACT WITH THE METAL SUBSTATE. THE AIM OF THIS STUDY WAS TO EVALUATE THE EFFECT OF VARYING EXPERIMENTAL PARAMETERS ON THE LOCALIZED CORROSION RESISTANCE OF AISI 316L STAINLESS STEEL. FOR THIS, SAMPLES WERE SUBMITTED TO SCANNING ELECTRON MICROSCOPY FOR MICROSTRUCTURAL CHARACTERIZATION. FOR ELECTROCHEMICAL CHARACTERIZATION, CYCLIC POLARIZATION TESTS WERE CARRIED OUT UNDER VARIOUS EXPERIMENTAL CONDITIONS, VARYING THE CHLORIDE CONCENTRATION, THE SCANNING CURRENT DENSITY AND THE POLARIZATION SCANNING SPEED. THE RESULTS SHOW THE INFLUENCE OF THE AGGRESSIVENESS OF CHLORIDE IONS IN SOLUTION AND THE IMPORTANCE OF THE CHARGE GENERATED DURING PITTING CORROSION FOR THE PHENOMENON OF REPASSIVATION. THE STUDY THUS VERIFIES THE EXPECTED EFFECT OF THESE EXPERIMENTAL VARIABLES ON THE LOCALIZED CORROSION OF AISI 316L STAINLESS STEEL.

Keywords

Corrosão; Aço inoxidável AISI 316L; Aço austenítico

Corrosion; Stainless Steel AISI 316L; Austenitic steels