AVALIAÇÃO DO PROCESSO DE CORROSÃO DO DIRECIONADOR DE FLUXO (CHICANA) DO RADIADOR DO TROCADOR DE CALOR DE UMA UNIDADE GERADORA DA USINA HIDRELÉTRICA DE TUCURUÍ

EVALUATION OF THE CORROSION PROCESS IN THE FLOW BAFFLE OF A RADIATOR WITHIN THE HEAT EXCHANGER OF A GENERATING UNIT AT THE TUCURUÍ HYDROELETRIC POWER PLANT

Authorship

NASCIMENTO, RITA DE KASSIA SILVA DO; SILVA, PATRICIA MAGALHÃES PEREIRA; GOMES, FERNANDO GAMA; PORFÍRIO, DARILENA MONTEIRO; MOREIRA, JULIO CEZAR FORNAZIER; ROCHA, OTÁVIO FERNANDES LIMA DA; DOERNER, FREDERICO RODOLFO PARENTE; ÁVILA, CAMILA CORASSA DE; LUCHETA, ADRIANO REIS; SILVA, PATRICIA MAGALHÃES PEREIRA; GOMES, FERNANDO GAMA

NASCIMENTO, RITA DE KASSIA SILVA DO

I am this author

SILVA, PATRICIA MAGALHÃES PEREIRA

I am this author

GOMES, FERNANDO GAMA

2 Articles, Downloaded 12 Times

PORFÍRIO, DARILENA MONTEIRO

I am this author

MOREIRA, JULIO CEZAR FORNAZIER

I am this author

ROCHA, OTÁVIO FERNANDES LIMA DA

I am this author

DOERNER, FREDERICO RODOLFO PARENTE

I am this author

ÁVILA, CAMILA CORASSA DE

I am this author

LUCHETA, ADRIANO REIS

I am this author

SILVA, PATRICIA MAGALHÃES PEREIRA

I am this author

GOMES, FERNANDO GAMA

I am this author

DOI

10.5151/2594-5327-41375

Downloads

Abstract

O OBJETIVO DESTE ESTUDO FOI ANALISAR OS PRODUTOS DE CORROSãO EM DIRECIONADORES DE FLUXO (CHICANA) DE LIGA DE ALUMíNIO, PROVENIENTE DO RADIADOR DO GERADOR NA UNIDADE GERADORA (UGH 07), DA USINA HIDRELéTRICA DE TUCURUí, NO ESTADO DO PARá, BRASIL. FORAM REALIZADAS ANáLISES METALOGRáFICAS, QUíMICAS E MICROESTRUTURAIS EM AMOSTRAS DE 10 X 10 CM³ CORTADAS DA CHICANA, INCLUINDO LIXAMENTO, POLIMENTO E ATAQUE QUíMICO COM OS REAGENTES NIDAL E KELLER. A COMPOSIçãO QUíMICA FOI DETERMINADA POR FLUORESCêNCIA DE RAIOS X (FRX) E A MICROESTRUTURA FOI EXAMINADA POR MICROSCOPIA óPTICA E ELETRôNICA DE VARREDURA (MEV), ENQUANTO OS PRODUTOS DE CORROSãO POR DIFRAçãO DE RAIOS X (DRX) E ESPECTROSCOPIA DE ENERGIA DISPERSIVA DE RAIOS X (EDS). OS RESULTADOS INDICARAM QUE AS CHICANAS SãO COMPOSTAS POR UMA LIGA AL-SI (80% AL E 17% SI, COM TRAçOS DE FE E MN), APRESENTANDO UMA MICROESTRUTURA DENDRíTICA COM INTERMETáLICOS QUE ACELERAM A CORROSãO. AS ANáLISES MINERALóGICAS REVELARAM A PRESENçA DE AL(OH)3 NOS PRODUTOS DE CORROSãO. CONCLUIU-SE QUE A LIGA DE ALUMíNIO UTILIZADA é INADEQUADA PARA O AMBIENTE OPERACIONAL DEVIDO à SUA SUSCEPTIBILIDADE à CORROSãO, RECOMENDANDO-SE A SUBSTITUIçãO MAIS FREQUENTE DAS DEFLETORAS DURANTE A MANUTENçãO PARA EVITAR FALHAS NO SISTEMA DE RESFRIAMENTO.

THE OBJECTIVE OF THIS STUDY WAS TO ANALYZE CORROSION PRODUCTS IN THE ALUMINUM BAFFLES OF THE GENERATOR RADIATOR IN ONE UNIT 07 OF THE TUCURUí HYDROELETRIC POWER PLANT, PARA STATE, BRAZIL. METALLOGRAPHIC, CHEMICAL, AND MICROSTRUCTURAL ANALYSES WERE PERFORMED ON 10 X 10 CM3 SAMPLES CUT FROM THE BAFFLE, INCLUDING GRINDING, POLISHING AND CHEMICAL ETCHING WITH NIDAL AND KELLER REAGENTS. CHEMICAL COMPOSITION WAS DETERMINED BY X-RAY FLUORESCENCE (XRF) AND MICROSTRUCTURE WAS EXAMINED BY OPTICAL AND SCANNING ELECTRON MICROSCOPY (SEM) WHILE THE CORROSION PRODUCTS WERE ANALYZED BY X-RAY DIFFRACTION (XRD) AND ENERGY DISPERSIVE X-RAY SPECTROSCOPY (EDS). THE RESULTS INDICATED THAT THE BAFFLES ARE COMPOSED OF AN AL-SI ALLOY (80% AL AND 17% SI, WITH TRACE OF FE AND MN, EXHIBITING A DENDRITIC MICROSTRUCTURE WITH INTERMETALLIC THAT ACCELERATE CORROSION. MINERALOGICAL ANALYSES REVEALED THE PRESENCE OF AL(OH)3 IN THE CORROSION PRODUCTS. IT WAS CONCLUDED THAT THE ALUMINUM ALLOY USED IS UNSUITABLE FOR THE OPERATING ENVIRONMENT DUE TO ITS SUSCEPTIBILITY TO CORROSION, RECOMMENDING MORE FREQUENT REPLACEMENT OF THE BAFFLES DURING MAINTENANCE TO AVOID COOLING SYSTEM FAILURES

Keywords

Chicanas; Trocador de Calor, Corrosão; Ligas Si-Al

Baffles; Heat Exchanger; Corrosion; Al-Si Alloy.