Title

AVALIAÇÃO DO RECOBRIMENTO CERÂMICO NA LIGA Ti-6Al-4V COM ESTRUTURA DE WIDMANSTÄTTEN

EVALUATION OF CERAMIC COATING ON THE Ti-6Al-4V ALLOY WITH WIDMANSTÄTTEN STRUCTURE

DOI

10.5151/2594-5327-16495

Downloads

Abstract

Este trabalho tem como objetivo avaliar o efeito do recobrimento cerâmico no comportamento em fluência na liga Ti-6Al-4V tratada termicamente com estrutura de Widmanstätten. Foi utilizada a liga Ti-6Al-4V na forma de barras cilíndricas, forjadas e recozidas a 190°C, durante 6 horas e resfriadas ao ar. A liga Ti-6Al-4V foi submetida a tratamento térmico na temperatura de 1.050°C por 30 minutos, com resfriamento ao forno até a temperatura de 700°C, mantendo-se nessa temperatura por 1 hora, seguido de resfriamento ao ar para obtenção da estrutura de Widmanstätten. Após tratamento térmico foi aplicado recobrimento cerâmico de CoNiCrAlY + ZrO2 por aspersão térmica. A liga Ti-6Al-4V, após tratamento térmico e com recobrimento cerâmico, foi submetida a ensaios de fluência a 600°C nas condições de 250 MP a e 319 MPa, na modalidade de carga constante. A liga com estrutura de Widmanstätten com recobrimento cerâmico apresenta maior resistência à fluência.

 

The aim of this paper is evaluate the effect of ceramic coating on creep behavior of Ti- 6Al-4V alloy with Widmanstätten structure. It was used a Ti-6Al-4V alloy in cylindrical bars forms, forged and annealed at 190°C for 6 hour s and cooled in air. The Ti-6Al-4V alloy was heat-treated at 1050°C for 30 minutes, cooled in furnace until 700°C and keeping in this temperature for 1 hour followed by air cooling in order to obtain Widmanstätten structure. After heat treatment it was applied ceramic coating of CoNiCrAlY + ZrO2 by plasma spray. The Ti-6Al-4V alloy after heat treatment and with ceramic coating was submitted to creep tests at 600°C and stress conditions of 250 and 319 MPa at constant load. The alloy with Widmanstätten structure and ceramic coating shows higher creep resistance.

Keywords

Fluência; Ti-6Al-4V; Tratamento térmico; Recobrimento cerâmico.

Creep; Ti-6Al-4V; Heat treatment; Ceramic coating.

How to refer

Briguente, Luciana Aparecida Narciso da Silva; Yogi, Lucila Mayumi; Sugahara, Tarcila; Reis, Danieli Aparecida Pereira; Neto, Carlos de Moura; Barboza, Miguel Justino Ribeiro. AVALIAÇÃO DO RECOBRIMENTO CERÂMICO NA LIGA Ti-6Al-4V COM ESTRUTURA DE WIDMANSTÄTTEN , p. 2560-2567. In: 65º Congresso ABM, Rio de Janeiro, 2010.