AVALIAÇÃO DOS MÉTODOS PARA QUANTIFICAÇÃO DA FRAÇÃO VOLUMÉTRICA DE MARTENSITA FORMADA DURANTE O PROCESSO DE LAMINAÇÃO A FRIO DO AÇO ASTM 201LN

EVALUATION OF QUANTIFICATION METHODS FOR MARTENSITE VOLUMETRIC FRACTION FORMED DURING THE COLD ROLLING PROCESS OF ON ASTM 201LN STEEL

Authorship

CORDEIRO, LEANDRA CARLA APARECIDA; ALVES, YURI MIKAEL DOS SANTOS; SILVA, CAROLLINE SERAFIM DA; SOUZA, CAMILA OLIVEIRA DE; MORAES, NÁHRIMA CHAMBELA; PAULA, ANDERSAN DOS SANTOS; BRANDÃO, LUIZ PAULO MENDONÇA

CORDEIRO, LEANDRA CARLA APARECIDA

I am this author

ALVES, YURI MIKAEL DOS SANTOS

I am this author

SILVA, CAROLLINE SERAFIM DA

I am this author

SOUZA, CAMILA OLIVEIRA DE

I am this author

MORAES, NÁHRIMA CHAMBELA

I am this author

PAULA, ANDERSAN DOS SANTOS

I am this author

BRANDÃO, LUIZ PAULO MENDONÇA

I am this author

DOI

10.5151/2594-5327-33443

Downloads

Abstract

Neste trabalho foram avaliados três métodos de quantificação da fração volumétrica de martensita ’ formada no aço ASTM 201LN durante o processo de laminação. Para isso, quatro amostras deste material foram laminadas à temperatura ambiente (~ 25 °C) com 8, 9, 10 e 11 passes de deformação com, aproximadamente, 10% de redução de espessura a cada passe. A quantificação de fases foi realizada por meio de ferritoscopia e por dois métodos a partir dos difratogramas de difração de Raios X (DRX): relação das áreas dos picos de maior intensidade e método de Rietveld. Os resultados obtidos da quantificação de fases pelos três métodos abordados mostraram que a fração volumétrica de martensita aumentou à medida que houve um aumento da deformação, embora os valores encontrados pela técnica de ferritoscopia foram inferiores que os obtidos pelos métodos de DRX. Isso pode ser explicado devido a erros inerentes à técnica de ferritoscopia, como também a técnica de ferritoscopia resultado de dados de volumes expressiva da amostra enquanto a DRX de uma camada inferior a 10 µm abaixo da superfície. Em relação aos valores obtidos pelos métodos de DRX, ambos apresentaram valores próximos, embora foi observado que o método de Rietveld foi considerado o mais preciso por apresentar valores de GOF (Goodness of fit) inferiores a 1,7, mostrando assim uma boa qualidade e precisão do refinamento.

In this work three methods of quantification of the martensite volumetric fraction formed in the ASTM 201LN steel during the rolling process were evaluated. To this end, four samples of this material were laminated at room temperature (~25 ° C) with 8, 9, 10 and 11 deformation passes with approximately 10% thickness reduction at each pass. Phase quantification was performed by means of a ferritoscopy and two methods from the XRD diffractograms: areas relation of the highest intensity peaks and Rielveld method. The obtained results of the phase quantification by the three methods presented showed that the volumetric fraction of martensite increased as there was an increase of the deformation, although the values found by the technique of ferritoscopy were lower than those obtained by the XRD methods. This can be explained due to errors inherent in the technique of Ferritoscopy, as well as the technique of ferritoscopy resulting from data of expressive volumes of the sample while the XRD of a layer less than 10 μm below the surface. Regarding the values obtained by the XRD methods, both presented close values, although it was observed that the Rietveld method was considered the most accurate because it presented values of GOF (Goodness of fit) of less than 1,7, thus showing a good quality and accuracy of refinement.

Keywords

Aço Inoxidável Austenítico, Efeito TRIP, Quantificação de fase, Martensita

Austenitic Stainless Steel; TRIP Effect; Phase quantification, Martensite