BASICIDADE BINÁRIA COMO PARÂMETRO DE QUALIDADE NO DESENVOLVIMENTO DE PELOTAS TIPO ALTO-FORNO

BINARY BASICITY AS QUALITY PARAMETER FOR DEVELOPING BLAST- FURNACE PELLETS

DOI

10.5151/2594-357X-23922

Downloads

Abstract

As qualidades física e metalúrgica das pelotas para alto-forno e redução direta são fortemente influenciadas pelas características dos minérios utilizados e, de maneira especial, pela basicidade binária, relação CaO/SiO2. Este trabalho mostra a influência da basicidade binária sobre a qualidade final de uma pelota de alto-forno produzida pela Vale S.A. As amostras geradas foram caracterizadas conforme os parâmetros físicos e metalúrgicos de rotina e também as propriedades de amolecimento e fusão. Análises microestruturais foram realizadas visando suportar o entendimento das variações de qualidade ocorridas nas diversas amostras. Observou-se que a resistência à compressão apresenta um valor máximo para basicidade em torno de 0,70, reduzindo significativamente em pelotas super ácidas, básicas e auto fundentes. Quanto aos parâmetros metalúrgicos e propriedades de amolecimento e fusão, foi observado um efeito positivo com o aumento da basicidade binária. A caracterização microestrutural das pelotas mostrou um aumento expressivo de macroporos com a elevação da basicidade binária, assim como o grau de maturação. O controle da basicidade binária da pelota se mostrou crítica no desenvolvimento de novos produtos.

 

The physical and metallurgical qualities of pellets for blast furnace and direct reduction processes are deeply affected by iron ore characteristics and, especially, the binary basicity, CaO/SiO2 ratio. This paper showed the influence of the binary basicity on the quality of fired pellets produced by Vale ́s pelletizing plant. Fired pellets samples were prepared and evaluated according to usually physical and metallurgical parameters and softening and melting properties. Micro structural analysis was carried out in order to support the understanding of quality variations. It was observed that compressive strength reached maximum value around 0.70 of binary basicity, decreasing significantly for acid, fluxed and self fluxed pellets. It was observed a positive effect of binary basicity on metallurgical, softening and melting properties. Micro structural evaluation showed a significant increase of micro and macro pores. The binary basicity control is a critical issue for developing new pellets.

Keywords

Pelota; Basicidade binária; Alto-forno; Microestrutura.

Pellets; Binary basicity; Blast furnace; Microstructure.

How to refer

Mafra, Washington Luiz; Resende, Valdirene Gonzaga de; Vieira, Maria Beatriz Harmendani; Domingues, Alei Leite Alcântara. BASICIDADE BINÁRIA COMO PARÂMETRO DE QUALIDADE NO DESENVOLVIMENTO DE PELOTAS TIPO ALTO-FORNO , p. 748-756. In: 43º Seminário de Redução de Minério de Ferro e Matérias-Primas e o 14º Simpósio Brasileiro de Minério de Ferro, São Paulo, 2013.