BIOCERâMICAS À BASE DE SILICATO DE MAGNÉSIO COM ADIÇÃO SEPARADA DE HIDROXIAPATITA E NIÓBIA

MAGNESIUM SILICATE-BASED BIOCERAMICS WITH SEPARATE ADDITIVES OF HYDROXYAPATITE AND NIOBIA

Authorship

FERBER, SAMUEL SOARES; NASCIMENTO, MARVIN DO; BARBOSA, CARLOS HENRIQUE DA LUZ; GARCIA, JULIANNA MAGALHÃES; SILVA, MARCELO HENRIQUE PRADO DA

FERBER, SAMUEL SOARES

I am this author

NASCIMENTO, MARVIN DO

I am this author

BARBOSA, CARLOS HENRIQUE DA LUZ

I am this author

GARCIA, JULIANNA MAGALHÃES

I am this author

SILVA, MARCELO HENRIQUE PRADO DA

I am this author

DOI

10.5151/2594-5327-41426

Downloads

Abstract

BIOCERâMICAS DERIVADAS DE SILICATO DE MAGNéSIO TêM ALCANçADO DESTAQUE COMO ALTERNATIVAS AOS FOSFATOS DE CáLCIO (COMO HIDROXIAPATITA), NO QUE SE REFERE A SEU USO EM REPARO óSSEO, DEVIDO AO PAPEL DESEMPENHADO POR íONS SI2+ E íONS MG2+ NESSE PROCESSO BIOLóGICO. NESSE SENTIDO, ESSE TRABALHO TEM POR OBJETIVO ANALISAR A BIOATIVIDADE DO SILICATO DE MAGNéSIO ADITIVADO COM DIFERENTES FRAçõES DE HIDROXIAPATITA E NIóBIA. PARA ISSO, A SíNTESE DO SILICATO DE MAGNéSIO FOI REALIZADA PELO MéTODO DE REAçãO DE ESTADO SóLIDO. A ADITIVAçãO COM HIDROXIAPATITA E NIóBIA (DOIS GRUPOS DIFERENTES MISTURADOS EM PORCENTAGEM EM PESO) FOI REALIZADA TAMBéM POR REAçãO DE ESTADO SóLIDO. O TESTE DE BIOATIVIDADE FOI REALIZADO COM A IMERSãO DAS AMOSTRAS EM UMA SOLUçãO DE SALIVA ARTIFICIAL. ESSES BIOMATERIAIS FORAM CARACTERIZADOS POR MEIO DE MICROSCOPIA ELETRôNICA DE VARREDURA COM FONTE DE EMISSãO DE CAMPO (MEV-FEG) E DIFRAçãO DE RAIOS X (DRX). POR FIM, OS RESULTADOS SUGEREM QUE O AUMENTO NO TEOR DE HIDROXIAPATITA AUMENTOU A BIOATIVIDADE DO MATERIAL; O MESMO NãO é VERDADE PARA A ADIçãO DE NIóBIA.

MAGNESIUM SILICATE-DERIVED BIOCERAMICS HAVE GAINED PROMINENCE AS ALTERNATIVES TO CALCIUM PHOSPHATES (SUCH AS HYDROXYAPATITE) FOR USE IN BONE REPAIR DUE TO THE ROLE PLAYED BY SI2+ AND MG2+ IONS IN THIS BIOLOGICAL PROCESS. IN THIS CONTEXT, THIS WORK AIMS TO ANALYZE THE BIOACTIVITY OF MAGNESIUM SILICATE DOPED WITH DIFFERENT FRACTIONS OF HYDROXYAPATITE AND NIOBIA. FOR THIS PURPOSE, THE SYNTHESIS OF MAGNESIUM SILICATE WAS CARRIED OUT BY THE SOLID-STATE REACTION METHOD. THE ADDITION OF HYDROXYAPATITE AND NIOBIA (TWO DIFFERENT GROUPS MIXED BY WEIGHT PERCENTAGE) WAS ALSO PERFORMED BY SOLID-STATE REACTION. THE BIOACTIVITY TEST WAS CONDUCTED BY IMMERSING THE SAMPLES IN AN ARTIFICIAL SALIVA SOLUTION. THESE BIOMATERIALS WERE CHARACTERIZED USING FIELD EMISSION SCANNING ELECTRON MICROSCOPY (FE-SEM) AND X-RAY DIFFRACTION (XRD). FINALLY, THE RESULTS SUGGEST THAT INCREASING THE HYDROXYAPATITE CONTENT INCREASED THE MATERIAL'S BIOACTIVITY; THE SAME IS NOT TRUE FOR THE ADDITION OF NIOBIA.

Keywords

Silicato de Magnésio; Nióbia; Hidroxiapatita; Bioatividade

Magnesium Silicate; Niobia; Hydroxyapatite; Bioactivity.