Caracterização microestrutural e avaliação de microdureza da junta soldada de aço SAE 1020 por soldagem MAG

Microstructural characterization and microhardness evaluation of a welded joint in SAE 1020 steel by MAG welding

Authorship

FERNANDEZ, CAMILA VASCONCELLOS; PAULA, WALTER LUÍS DE SOUZA CHAGAS DE; JACINTHO, PABLO BARBOSA; AZEVEDO, JOSSANDRO DA SILVA DE; GOMES, ALZIMAR FERNANDES; CHAGAS, FABIANO PORTAL; MENDES, SILVIO GONÇALVES; SOUZA, LUCAS MENEZES DE; PEREIRA, ELAINE CRISTINA

FERNANDEZ, CAMILA VASCONCELLOS

I am this author

PAULA, WALTER LUÍS DE SOUZA CHAGAS DE

I am this author

JACINTHO, PABLO BARBOSA

I am this author

AZEVEDO, JOSSANDRO DA SILVA DE

I am this author

GOMES, ALZIMAR FERNANDES

I am this author

CHAGAS, FABIANO PORTAL

I am this author

MENDES, SILVIO GONÇALVES

I am this author

SOUZA, LUCAS MENEZES DE

I am this author

PEREIRA, ELAINE CRISTINA

I am this author

DOI

10.5151/2594-5327-43818

Downloads

Abstract

Este trabalho teve como objetivo caracterizar microestruturamente e avaliar a microdureza de uma junta soldada em aço SAE 1020 obtida pelo processo MAG. As amostras foram soldadas em junta de topo, utilizando arame ER70S‑6, gás de proteção CO₂, tensão de 17 V e velocidade de alimentação do arame de 6 m/min, sem aplicação de tratamentos térmicos. A caracterização incluiu ensaio de líquido penetrante, análise metalográfica e ensaio de microdureza Vickers. Os resultados evidenciaram microestrutura ferrita‑perlita no metal de base e a formação de ferrita acicular e ferrita de Widmanstätten na zona termicamente afetada e na zona de fusão. Os valores médios de microdureza foram da ordem de 152 HV, com valores superiores na ZTA direita (175 HV) e redução significativa na amostra 2, atingindo 105 HV na ZTA e 97 HV na ZF, associados ao maior aporte térmico e menor taxa de resfriamento decorrentes das condições de soldagem.

This study aimed to perform a microstructural characterization and microhardness evaluation of a welded joint in SAE 1020 steel obtained by the MAG welding process. The samples were welded in a butt joint configuration using ER70S‑6 filler wire, CO₂ shielding gas, a voltage of 17 V, and a wire feed speed of 6 m/min, without post-weld heat treatment. The characterization included liquid penetrant testing, metallographic analysis, and Vickers microhardness testing. The results revealed a ferrite–pearlite microstructure in the base metal and the formation of acicular ferrite and Widmanstätten ferrite in the heat-affected zone and fusion zone. The average microhardness values were around 152 HV, with higher values in the right heat-affected zone (175 HV) and a significant reduction in sample 2, reaching 105 HV in the HAZ and 97 HV in the fusion zone, associated with higher heat input and lower cooling rates resulting from the welding conditions..

Keywords

Soldagem MAG, Aço SAE 1020, Microestrutura, Microdureza

MAG Welding, SAE 1020 Steel, Microstructure, Microhardness