Title

CARACTERIZAÇÃO DA LIGA DE ALUMÍNIO 4032 APÓS CONFORMAÇÃO POR EXTRUSÃO

CHARACTERIZATION OF ALUMINIUM ALLOY 4032 AFTER EXTRUSION FORMING

Authorship

MACIEIRA, KARINA CARBONE; FILHO, ANIBAL DE ANDRADE MENDES

MACIEIRA, KARINA CARBONE

I am this author

FILHO, ANIBAL DE ANDRADE MENDES

I am this author

DOI

10.5151/2594-5327-41102

Downloads

Abstract

A LIGA DE ALUMíNIO 4032 POSSUI BOA ESTABILIDADE TéRMICA, ELEVADA RESISTêNCIA à CORROSãO E AO DESGASTE. É UTILIZADA EM PEçAS AUTOMOTIVAS QUE TRABALHAM EM ALTAS TEMPERATURAS E SOB SOLICITAçãO MECâNICA SEVERA. NO PRESENTE TRABALHO FOI REALIZADA A CARACTERIZAçãO MECâNICA E METALOGRáFICA DE QUATRO CONDIçõES DESTA LIGA: HOMOGENEIZADA ANTES DA DEFORMAçãO PLáSTICA, PERFIL CONFORMADO POR EXTRUSãO, PERFIL EXTRUDADO E RECOZIDO E PERFIL EXTRUDADO NA CONDIçãO T6. FOI POSSíVEL OBSERVAR A EVOLUçãO MICROESTRUTURAL E DAS PROPRIEDADES MECâNICAS DA LIGA APóS A CONFORMAçãO PLáSTICA E APóS OS TRATAMENTOS TéRMICOS. NA MICROESTRUTURA, é NOTáVEL A REDUçãO DO TAMANHO DAS PARTíCULAS DE SEGUNDA FASE E PRECIPITADOS E TAMBéM A MELHORA NA DISTRIBUIçãO DELES. COM RELAçãO àS PROPRIEDADES MECâNICAS, FICA EXPLíCITO DOIS GRANDES SALTOS NO LIMITE DE RESISTêNCIA à TRAçãO: APóS CONFORMAçãO PLáSTICA, ONDE ATINGE 200 MPA, E APóS TRATAMENTO TéRMICO T6, ONDE ATINGE 363 MPA.

ALUMINUM ALLOY 4032 HAS A GOOD THERMAL STABILITY, HIGH CORROSION AND WEAR RESISTANCE. IT IS USED IN AUTOMOTIVE PARTS THAT WORK AT HIGH TEMPERATURES AND UNDER SEVERE MECHANICAL STRESS. IN THIS WORK, MECHANICAL AND METALLOGRAPHIC CHARACTERIZATION WAS CARRIED OUT CONSIDERING FOUR CONDITIONS: HOMOGENIZED MATERIAL BEFORE PLASTIC DEFORMATION, EXTRUSION-FORMED PROFILE, EXTRUDED AND ANNEALED PROFILE, AND EXTRUDED PROFILE IN T6 CONDITION. IT WAS POSSIBLE TO OBSERVE THE MICROSTRUCTURAL AND MECHANICAL PROPERTIES EVOLUTION OF THE ALLOY AFTER PLASTIC DEFORMATION AND HEAT TREATMENT. THE MICROSTRUCTURE SHOWS A NOTICEABLE REDUCTION IN THE SIZE OF THE SECOND PHASE PARTICLES AND PRECIPITATES, AS WELL AS AN IMPROVEMENT IN THEIR DISTRIBUTION. IN TERMS OF MECHANICAL PROPERTIES, TWO BIG LEAPS IN THE TENSILE STRENGTH LIMIT CAN BE SEEN: AFTER PLASTIC FORMING, WHERE IT REACHES 200 MPA, AND AFTER HEAT TREATMENT IN T6 TEMPER, WHERE IT REACHES 363 MPA.

Keywords

AA4032; Extrusão; Tratamento Térmico; Metalografia

AA4032; Extrusion; Heat Treatment; Metallography