CARACTERIZAÇÃO DA RESPOSTA MAGNÉTICA DE UM AÇO INOXIDÁVEL AUSTENÍTICO TIPO HP- NBTI EM DIFERENTES CONDIÇÕES MICROESTRUTURAIS POR MICROSCOPIA MAGNETO-ÓTICA KERR.

MAGNETIC RESPONSE CHARACTERIZATION OF AN AUSTENITIC STAINLESS STELL HP-NBTI TYPE IN DIFFERENT MICROSTRUCTURAL CONDITIONS BY KERR MAGNETO-OPTIC MICROSCOPY.

Authorship

Neves, Thiago Tôrres Matta; Santos, Milena Gonçalves dos; Pacheco, Clara Johanna; Mendes, Matheus Campolina; Almeida, Luiz Henrique de; Pereira, Gabriela Ribeiro

DOI

10.5151/2594-5327-34987

Downloads

heading.download_article_detail 8 Downloads

Abstract

AÇOS AUSTENÍTICOS HP MODIFICADOS SÃO EMPREGADOS NA PRODUÇÃO DE TUBOS DE REFORMA À VAPOR DEVIDO A SUA RESISTÊNCIA, SOBRETUDO À FLUÊNCIA EM ALTAS TEMPERATURAS. DURANTE A OPERAÇÃO ESTES TUBOS SOFREM OS EFEITOS DO ENVELHECIMENTO DE ACORDO COM A TEMPERATURA A QUE SÃO EXPOSTOS, ESTAS MODIFICAÇÕES SÃO CLASSIFICADAS COMO ESTADOS DE EVOLUÇÃO MICROESTRUTURAL. COM A FINALIDADE DE CARACTERIZAR MAGNETICAMENTE O MATERIAL, NESTE TRABALHO, FOI USADA A TÉCNICA DE MICROSCOPIA MAGNETO-ÓTICA KERR NO MODO QUALITATIVO, POR MEIO DE IMAGENS E QUANTITATIVO, ATRAVÉS DO LEVANTAMENTO DAS CURVAS DE HISTERESE. ESTES RESUSTADOS SÃO IMPORTANTES PARA O DESENVOLVIMENTO DE METODOLOGIAS DE ENSAIOS NÃO DESTRUTIVOS UTILIZANDO CORRENTES PARASITAS. FORAM ANALISADAS DUAS AMOSTRAS DE AÇO HP-NBTI CLASSIFICADAS COMO ESTADO I E V DE EVOLUÇÃO MICROESTRUTURAL, RETIRADAS DE UM TUBO QUE ESTEVE EM OPERAÇÃO POR 90.000H. AS AMOSTRAS FORAM ANALISADAS UTILIZANDO MEV E EDS A FIM DE IDENTIFICAR AS FASES PRESENTES EM CADA CONDIÇÃO. UMA VEZ DETERMINADAS FOI POSSÍVEL IDENTIFICAR A RESPOSTA MAGNÉTICA NA PAREDE EXTERNA DO TUBO, INDICANDO A PRESENÇA DE UM COMPORTAMENTO FERROMAGNÉTICO TANTO NA AMOSTRA CLASSIFICADA COMO ESTADO I DE EVOLUÇÃO MICROESTRUTURAL, QUANTO NA AMOSTRA DE ESTADO V.

 

MODIFIED HP AUSTENITIC STEELS ARE USED IN THE PRODUCTION OF STEAM REFORM TUBES DUE TO THEIR RESISTANCE, ESPECIALLY TO CREEP AT HIGH TEMPERATURES. DURING OPERATION, THESE TUBES ARE AFFECTED BY THE AGING ACCORDING TO THE TEMPERATURE TO WHICH THEY ARE EXPOSED. THESE CHANGES ARE CLASSIFIED AS STATES OF MICROSTRUCTURAL EVOLUTION. IN ORDER TO MAGNETICALLY CHARACTERIZE THE MATERAIL, IN THIS STUDY IT WAS UTILIZED THE KERR MAGNETO-OPTIC MICROSCOPY TECHNIQUE IN A QUALITATIVE WAY, THROUGH IMAGES AND QUANTITATIVELY, THROUGH THE STUDY OF HYSTERESIS CURVES. THESE RESULTS ARE IMPORTANT TO THE DEVELOPMENT OF METHODOLOGIES OF NON-DESTRUCTIVE TESTING USING EDDY CURRENTS. IN THIS WORK, TWO SAMPLES OF HP-NBTI STEEL CLASSIFIED AS A STATE I AND V OF MICROSTRUCTURAL EVOLUTION WERE ANALYZED, TAKEN FROM A TUBE THAT WAS IN OPERATION FOR 90,000H. THE SAMPLES WERE ANALYZED USING SEM AND EDS TO IDENTIFY THE PHASES PRESENT IN EACH CONDITION. ONCE DETERMINED, IT WAS POSSIBLE TO IDENTIFY THE MAGNETIC RESPONSE ON THE OUTER WALL OF THE TUBE, INDICATING THE PRESENCE OF A FERROMAGNETIC BEHAVIOR BOTH IN THE SAMPLE CLASSIFIED AS THE STATE I OF MICROSTRUCTURAL EVOLUTION, AND IN THE SAMPLE OF STATE V.