Title

CARACTERIZAÇÃO DAS MICROESTRUTURAS E DA RESISTÊNCIA A CORROSÃO DE REVESTIMENTOS DA MISTURA DAS LIGAS DE NÍQUEL AWS ERNiCrMo - 3 E AWS ERNiCrMo - 4 SOLDADOS PELO PROCESSO MIG/MAG DUPLO ARAME

MICROSTRUCTURAL AND CORROSION CHARACTERIZATION OF THE WELDING OVERLAY THE MIX THE ALLOYS AWS ERNiCrMo - 3 E AWS ERNiCrMo - 4 WITH MIG/MAG DOUBLE WIRE

Authorship

Kamilla Giló Santiago; Marcelo Ferreira Motta; Cleiton Carvalho Silva; Jamil Nobre de Castro; Igor Paulino Fernandes; Eduvânio Machado Silva Júnior

Kamilla Giló Santiago

I am this author

Marcelo Ferreira Motta

I am this author

Cleiton Carvalho Silva

I am this author

Jamil Nobre de Castro

I am this author

Igor Paulino Fernandes

I am this author

Eduvânio Machado Silva Júnior

I am this author

DOI

10.5151/1516-392X-24475

Downloads

Abstract

Nesse trabalho para caracterização metalúrgica dos revestimentos compostos pela mistura das ligas AWS ERNiCrMo - 3 E AWS ERNiCrMo - 4 soldados pelo processo MIG/MAG duplo arame foram realizadas análises micrográficas por meio de microscopia eletrônica de varredura. Observou-se semelhança entre os precipitados do topo e da interface do metal de solda com o substrato e que a microestrutura obtida com a soldagem das duas ligas, simultaneamente, resultou na mistura das microestruturas, obtidas a partir das soldagens com cada uma das ligas de forma isolada. O ensaio para avaliação do desempenho da mistura quanto à resistência a corrosão foi realizado conforme a norma ASTM - G 48, método C para determinação da temperatura crítica de pite da mistura das ligas. Foram utilizadas amostras dos revestimentos com maior e menor diluição. O resultado do ensaio apontou que os revestimentos soldados apresentaram temperatura crítica de pite superior ao da liga AWS ERNiCrMo-3 e semelhante ao da liga AWS ERNiCrMo-4.

In this work for metallurgical characterization of welding overlays composed by the mixture of alloys ERNiCrMo AWS–3 and AWS ERNiCrMo-4 welded by MIG / MAG double wire process, micrographic analyzes were performed by means of scanning electron microscopy (SEM). Similarity was observed between the precipitates at the top of the weld metal and in the interface with the substrate. The microstructure obtained by welding two alloys of both resulted in a mixture of microstructures obtained from welds with each alloy isolation. The test for evaluating the performance of the mixture for resistance to corrosion was performed according to ASTM - G 48, C method to determine the critical pitting temperature of the mixture of alloys. Samples of coatings with higher and lower dilution were used. The test result showed that the welded coating had higher critical pitting temperature than the alloy AWS ERNiCrMo-3 and similar to Alloy AWS ERNiCrMo-4.

Keywords

Superligas de níquel; Corrosão

Superalloys based nickel; Corrosion