CARACTERIZAÇÃO DE FILMES ANÓDICOS NANOTUBULARES CRESCIDOS EM LIGAS DE TITÂNIO.

CHARACTERIZATION OF NANOTUBULAR ANODIC FILMS GROWN ON TITANIUM ALLOYS.

Authorship

NOVAES, FREDERICO GOTSCHALG MAIA SILVA; NOVAES, FREDERICO GOTSCHALG MAIA SILVA

NOVAES, FREDERICO GOTSCHALG MAIA SILVA

I am this author

NOVAES, FREDERICO GOTSCHALG MAIA SILVA

I am this author

DOI

10.5151/2594-4711-40746

Downloads

Abstract

O OBJETIVO DESTE TRABALHO FOI CARACTERIZAR CAMADAS ANODIZADAS DE LIGAS DE TITâNIO E DE NITI . FORAM CRESCIDOS POR ANODIZAçãO ELETROQUíMICA FILMES DE óXIDO EM TITâNIO PURO E EM LIGA DE NITI . UMA CARACTERIZAçãO MORFOLóGICA, QUíMICA E ESTRUTURAL FOI REALIZADA PARA AVALIAR AS APLICAçõES POTENCIAIS DESTES FILMES. A ANáLISE MORFOLóGICA FOI CONDUZIDA POR MEV DE ALTA RESOLUçãO. A COMPOSIçãO QUíMICA SUPERFICIAL FOI MEDIDA POR ENERGIA DISPERSIVA DE RAIOS X (EDS). O PERFIL DE COMPOSIçãO DA CAMADA ANODIZADA BEM COMO SUA ESPESSURA FORAM DETERMINADOS UTILIZANDO UMA SISTEMA GDOES. A ESTRUTURA CRISTALINA DAS CAMADAS ANODIZADAS FOI AVALIADA POR DIFRAçãO DE RAIOS X ANTES E APóS TRATAMENTO DE RECOZIMENTO DAS AMOSTRAS ANODIZADAS. OS RESULTADOS MOSTRARAM UMA MORFOLOGIA NANOTUBULAR PARA AS CAMADAS ANODIZADAS EM AMBAS AS LIGAS, CONSTATANDO-SE NANOTUBOS COM MAIORES DIâMETROS E MAIOR ESPESSURA NA LIGA DE TI QUANDO COMPARADO COM A LIGA DE NITI. AS CAMADAS ANODIZADAS ESTãO CONSTITUíDAS DE óXIDOS DE TITâNIO E DE óXIDOS DE NI E TI, PARA AS AMOSTRAS DE TI E NITI, RESPECTIVAMENTE. OS RESULTADOS OBTIDOS SUGEREM A UTILIZAçãO DAS SUPERFíCIES ANODIZADAS COMO FOTOCATALISADORES PARA USO NO SEGMENTO DA ENERGIA E DO MEIO AMBIENTE .

THE OBJECTIVE OF THIS WORK WAS TO CHARACTERIZE ANODIZED LAYERS OF TITANIUM AND NITI ALLOYS. OXIDE FILMS WERE GROWN ON PURE TITANIUM AND NITI ALLOY BY ELECTROCHEMICAL ANODIZATION. A MORPHOLOGICAL, CHEMICAL AND STRUCTURAL CHARACTERIZATION WAS CARRIED OUT TO EVALUATE THE POTENTIAL APPLICATIONS OF THESE FILMS. MORPHOLOGICAL ANALYSIS WAS CONDUCTED USING HIGH-RESOLUTION SEM. THE SURFACE CHEMICAL COMPOSITION WAS MEASURED BY ENERGY DISPERSIVE X-RAY (EDS). THE COMPOSITION PROFILE OF THE ANODIZED LAYER AS WELL AS ITS THICKNESS WERE DETERMINED USING A GDOES SYSTEM. THE CRYSTALLINE STRUCTURE OF THE ANODIZED LAYERS WAS EVALUATED BY X-RAY DIFFRACTION BEFORE AND AFTER ANNEALING TREATMENT OF THE ANODIZED SAMPLES. THE RESULTS SHOWED A NANOTUBULAR MORPHOLOGY FOR THE ANODIZED LAYERS IN BOTH ALLOYS, WITH NANOTUBES WITH LARGER DIAMETERS AND GREATER THICKNESS IN THE TI ALLOY WHEN COMPARED TO THE NITI ALLOY. THE ANODIZED LAYERS ARE MADE UP OF TITANIUM OXIDES AND NI AND TI OXIDES, FOR THE TI AND NITI SAMPLES, RESPECTIVELY. THE RESULTS OBTAINED SUGGEST THE USE OF ANODIZED SURFACES AS PHOTOCATALYSTS FOR USE IN THE ENERGY AND ENVIRONMENTAL SEGMENT.