Title

CARACTERIZAÇÃO DE MATERIAIS COMPÓSITOS DE MATRIZ POLIÉSTER E FIBRAS DE SISAL COM COMPRIMENTO HÍBRIDO DE 5 A 15 mm

CHARACTERIZATION MATRIX COMPOSITE MATERIALS AND POLYESTER SISAL FIBER LENGTH WITH HYBRID OF 5 TO 15 mm1

DOI

10.5151/2594-5327-22981

Downloads

Abstract

A utilização de materiais naturais, provenientes de fontes renováveis, apresenta diversas vantagens quando comparados com materiais de fontes não renováveis. Dentre os materiais naturais encontram-se as fibras vegetais que fazem parte da paisagem de diversos países e que no Brasil podem ser encontrados diversos tipos; como por exemplo, o sisal. Neste artigo foi produzido compósitos reforçados com fibras de sisal de comprimentos híbrido variando de 5 mm a 15 mm. As fibras foram cortadas com o uso de um moinho granulador. Foram fabricados oito corpos de prova para cada fração mássica definida com as seguintes proporções; 3,90%, 4,87% e 5,41%; a fabricação foi realizada por moldagem manual, sem pressão ou compactação, usando resina poliéster insaturada com a proporção de agente de cura/resina de 0,33%. O resultados da resistência a tração dos compósitos de sisal de fração mássica 3,90% foi de 16,23 MPa; e de fração mássica 4,87% foi de 19,64 MPa; e de fração mássica 5,41% foi de 22,83 MPa. Os resultados mostraram que os compósitos de fração mássica 5,41% de melhor resistência mecânica. As fraturas dos compósitos foram verificadas por microscopia eletrônica de varredura (MEV), onde identificadas as disposição das fibras nos compósitos.

 

The use of natural materials from renewable resources, has several advantages when compared to non-renewable materials. Among the natural materials are vegetable fibers that part of the landscape from various countries and which can be found in Brazil different types; such as sisal. This article was produced fiber-reinforced composite sisal hybrid lengths ranging from 5 mm to 15 mm. The fibers were cut using a mill granulator. Were made eight specimens for each mass fraction defined with the following proportions; 3.90%, 4.87% and 5.41%, manufacturing was done by hand molding, without pressure or compression, using polyester resin unsaturated with the ratio of curing agent / resin 0.33%. The results of the tensile strength of the composites of sisal mass fraction of 3.90% was 16.23 MPa, and mass fraction of 4.87% was 19.64 MPa, and mass fraction of 5.41% was 22.83 MPa. The results showed that the composites of 5.41% mass fraction better mechanical strength. Fractures of the composites were observed by scanning electron microscopy (SEM), which identified the arrangement of fibers in composites.

Keywords

Fibras de sisal; Fração de fibras; Materiais compósitos.

Sisal fibers; Fraction of fibers; Composite materials.