CARACTERIZAÇÃO DE MEMBRANA COMPÓSITO BASE PVA/ÓXIDO DE GRAFENO PARA CÉLULA A COMBUSTÍVEL

CHARACTERIZATION OF PVA/GRAPHENE OXIDE-BASED COMPOSITE MEMBRANE FOR FUEL CELL

Authorship

TEIXEIRA, BRITNEY APARECIDA; SILVA, MARIANGELA PEREIRA DA; MAIA, PAULO JOSÉ DE SOUSA; BRUM, FÁBIO JOSÉ BENTO

TEIXEIRA, BRITNEY APARECIDA

I am this author

SILVA, MARIANGELA PEREIRA DA

I am this author

MAIA, PAULO JOSÉ DE SOUSA

I am this author

BRUM, FÁBIO JOSÉ BENTO

I am this author

DOI

10.5151/2594-4711-41492

Downloads

Abstract

NESTE TRABALHO FORAM APRESENTADOS OS RESULTADOS DA CARACTERIZAçãO DE MEMBRANAS CATIôNICAS COMPóSITO BASE PVA COM DIFERENTES CONCENTRAçõES DE óXIDO DE CARBONO E SUA PERFORMANCE APLICADA EM PROTóTIPO DE CéLULA A COMBUSTíVEL. FORAM PREPARADAS MEMBRANAS COM TRêS CONCENTRAçõES DIFERENTES DE óXIDO DE GRAFENO (GO). A CARACTERIZAçãO DAS MEMBRANAS SE DEU POR MICROSCOPIA DE FORçA ATôMICA PARA VERIFICAR A MORFOLOGIA DAS MEMBRANAS QUANDO HIDRATADAS, A RESISTêNCIA TéRMICA DAS MEMBRANAS FOI AVALIADA POR ANáLISE TERMOGRAVIMéTRICA, A CONDUTIVIDADE IôNICA DAS MEMBRANAS FOI ANALISADA POR IMPEDâNCIA COMPLEXA. NO TESTE EM PROTóTIPO DE CéLULA A COMBUSTíVEL A MEMBRANA COMPóSITO APRESENTOU 0,6 V DE POTENCIAL DE CIRCUITO ABERTO E POTêNCIA DE 0,18 W COMPARADA, A MEMBRANA NAFION COM 0,8 V DE CIRCUITO ABERTO E 0,12 W DE POTêNCIA NAS CONDIçõES DE ENSAIO NA CéLULA.

IN THIS WORK, THE RESULTS OF THE CHARACTERIZATION OF PVA-BASED COMPOSITE CATIONIC MEMBRANES WITH DIFFERENT CONCENTRATIONS OF GRAPHENE OXIDE AND THEIR PERFORMANCE WHEN APPLIED IN A FUEL CELL PROTOTYPE WERE PRESENTED. MEMBRANES WITH THREE DIFFERENT CONCENTRATIONS OF GRAPHENE OXIDE (GO) WERE PREPARED. THE CHARACTERIZATION OF THE MEMBRANES WAS PERFORMED USING ATOMIC FORCE MICROSCOPY TO VERIFY THE MORPHOLOGY OF THE MEMBRANES WHEN HYDRATED. THE THERMAL RESISTANCE OF THE MEMBRANES WAS EVALUATED BY THERMOGRAVIMETRIC ANALYSIS, AND THE IONIC CONDUCTIVITY OF THE MEMBRANES WAS ANALYZED BY COMPLEX IMPEDANCE. IN THE FUEL CELL PROTOTYPE TEST, THE COMPOSITE MEMBRANE SHOWED AN OPEN CIRCUIT POTENTIAL OF 0.6 V AND A POWER OF 0.18 W, COMPARED TO THE NAFION MEMBRANE WITH AN OPEN CIRCUIT POTENTIAL OF 0.8 V AND A POWER OF 0.12 W UNDER THE TEST CONDITIONS IN THE CELL.

Keywords

Membrana catiônica; Célula a combustível; Óxido de grafeno; Poli(álcool vinílico).

Proton exchange membrane fuel cell (PEMFC); Fuel cell; Graphene oxide (GO); Poly(vinyl alcohol).