Title

CARACTERIZAÇÃO DE PEÇAS POROSAS NANOESTRUTURADAS DE FERRITA DE NÍQUEL

CHARACTERIZATION OF NANOSTRUCTURED POROUS NICKEL FERRITE PARTS

Authorship

RIBEIRO, JULIANA LOPES; FARIA, SABRINA COSTA; ALVES, DIEGO DOS SANTOS; CARVALHO, BRUNO CRISTIAN MELLO; JÚNIOR, EUSTÁQUIO DE SOUZA BAÊTA; AGUILERA, LETICIA DOS SANTOS; MORAES, FELLIPE DE SÁ

RIBEIRO, JULIANA LOPES

I am this author

FARIA, SABRINA COSTA

I am this author

ALVES, DIEGO DOS SANTOS

I am this author

CARVALHO, BRUNO CRISTIAN MELLO

I am this author

JÚNIOR, EUSTÁQUIO DE SOUZA BAÊTA

I am this author

AGUILERA, LETICIA DOS SANTOS

38 Articles, Downloaded 234 Times

MORAES, FELLIPE DE SÁ

I am this author

DOI

10.5151/2594-4711-40860

Downloads

Abstract

CONFORMAçãO DE PEçAS CERâMICAS POROSAS POR CONGELAMENTO TEM COMO DESAFIO O CONTROLE DE PARâMETROS, COMO CONCENTRAçãO DE SóLIDOS, TIPO DE SOLVENTE, TIPO E CONCENTRAçãO DE ADITIVOS E TEMPOS E TEMPERATURAS DE PROCESSOS TéRMICOS ENVOLVIDOS. O PRESENTE ARTIGO TEVE COMO FOCO PRINCIPAL A SíNTESE E CARACTERIZAçãO DA FERRITA DE NíQUEL APóS PROCESSAMENTO POR FREEZE CASTING. AS AMOSTRAS FORAM CONGELADAS, LIOFILIZADAS E SINTERIZADAS E A MACROESTRUTURA POROSA E AS CARACTERíSTICAS CERâMICAS DAS PEçAS FORAM INVESTIGADAS POR MICROSCOPIA ELETRôNICA DE VARREDURA (MEV) E MéTODO DE ARQUIMEDES, COMPARANDO VARIAçãO DE 3 LIGANTES POLIMéRICOS, PEG-400, 1500 E 4000, NA CONCENTRAçãO DE 4%. FOI OBSERVADO QUE AS AMOSTRAS OBTIVERAM ESTRUTURA POROSA EM ZONAS DE CONGELAMENTO DISTINTAS, CARACTERíSTICAS DE TAXAS DE RESFRIAMENTO MUITO ALTAS. ALéM DISSO, A AMOSTRA PROCESSADA COM PEG-4000 APRESENTOU MAIORES CRESCIMENTOS DE GRãOS E DIMINUIçãO DE POROS, EM RELAçãO AS AMOSTRAS COM PEG-400 E 1500. A POROSIDADE APARENTE DAS TRêS VARIAçõES DE ADITIVOS FICOU EM TORNO DE 50% E UMA BAIXA DENSIFICAçãO DA ORDEM DE 30%.

THE CHALLENGE OF FORMING POROUS CERAMIC PARTS BY FREEZING IS ON CONTROLLING PARAMETERS, SUCH AS SOLIDS CONCENTRATION, TYPE OF SOLVENT, TYPE AND CONCENTRATION OF ADDITIVES AND TIMES AND TEMPERATURES OF THE THERMAL PROCESSES INVOLVED. THE MAIN FOCUS OF THIS ARTICLE WAS THE SYNTHESIS AND CHARACTERIZATION OF NICKEL FERRITE AFTER PROCESSING BY FREEZE CASTING. THE SAMPLES WERE FROZEN, FREEZE-DRIED AND SINTERED AND THE POROUS MACROSTRUCTURE AND CERAMIC CHARACTERISTICS OF THE PIECES WERE INVESTIGATED BY SCANNING ELECTRON MICROSCOPY (SEM) AND ARCHIMEDES METHOD, COMPARING VARIATION OF 3 POLYMERIC BINDERS, PEG-400, 1500 AND 4000, IN CONCENTRATION OF 4%. IT WAS OBSERVED THAT THE SAMPLES OBTAINED A POROUS STRUCTURE IN DISTINCT SOLIDIFICATION ZONES, CHARACTERISTIC OF VERY HIGH COOLING RATES. FURTHERMORE, THE SAMPLE PROCESSED WITH PEG- 4000 SHOWED GREATER GRAIN GROWTH AND REDUCED PORES, COMPARED TO THE SAMPLES WITH PEG-400 E 1500. THE APPARENT POROSITY OF THE THREE ADDITIVE VARIATIONS WAS AROUND 50% AND A LOW DENSIFICATION OF THE ORDER OF 30%.

Keywords

Ferrita de níquel; Síntese; Freeze-casting; PEG.

Nickel ferrite; Synthesis; Freeze-casting; PEG.