CARACTERIZAÇÃO DE SÍNTER POR MICROSCOPIA ÓTICA DIGITAL E ANÁLISE DE IMAGENS

IRON ORE SINTER CHARACTERIZATION THROUGH DIGITAL OPTICAL MICROSCOPY AND IMAGE ANALYSIS

Authorship

Schinazi, Gustavo; Gomes, Otávio da Fonseca Martins; Paciornik, Sidnei; Vieira, Maria Beatriz; Iglesias, Julio Cesar Alvarez

Schinazi, Gustavo

I am this author

Gomes, Otávio da Fonseca Martins

I am this author

Paciornik, Sidnei

I am this author

Vieira, Maria Beatriz

I am this author

Iglesias, Julio Cesar Alvarez

I am this author

DOI

10.5151/2594-357X-15792

Downloads

Abstract

Neste trabalho, propõe-se uma metodologia para a caracterização microestrutural quantitativa de sínter de minério de ferro. Amostras de sínter com cerca de 3 cm foram embutidas em resina, lixadas e polidas. Para cada seção polida, foram adquiridas imagens em mosaico cobrindo toda a área da seção (lente objetiva de 5X). Uma rotina automática analisou as imagens, medindo as frações de área de cada fase, inclusive poros. Além disso, para comparação, foram também adquiridas e analisadas cerca de 2.000 imagens de campos em mais alta resolução (objetiva de 20X). As frações de fase foram também obtidas por difratometria de raios-x utilizando o método de Rietveld. Os resultados obtidos em diferentes resoluções foram bem semelhantes para as fases hematita, magnetita e ferritos. Contudo, houve uma grande discrepância, cerca de 40% de erro relativo, nas medidas dos silicatos. Da mesma forma, os resultados independentemente obtidos por difratometria de raios-x foram consistentes com as medidas por análise de imagens, com exceção dos silicatos.

A methodology for quantitative microstructural characterization of iron ore sinters was proposed. Sinter samples with ≈3 cm diameter were mounted in resin, ground and polished. For each sample, mosaic images covering the entire sample were acquired (5X objective lens). An automatic image analysis routine was employed to measure the area fraction of each phase, including pores. In addition, 2000 images were also acquired and analyzed in higher resolution (20X objective). The phase fractions were also obtained by X-ray diffraction using the Rietveld method. The results obtained from different resolutions were very similar for hematite, magnetite and ferrites. However, there was a wide variation, about 40%, in silicates fractions. Likewise, the X-ray diffraction results were consistent with the measurements carried out by image analysis, except for silicates.

Keywords

Sínter; Minério de ferro; Microscopia digital; Análise de imagens.

Sinter; Iron ore; Digital microscopy; Image analysis.