CARACTERIZAÇÃO DO COMPORTAMENTO MECÂNICO DO AÇO H13 COM TRATAMENTO DUPLEX

MECHANICAL CHARACTERIZATION OF H13 STEEL WITH DUPLEX TREATMENT

Authorship

Suzuki, Luciane Yumi; Bassani, Irionson Antônio; Torresi, Ricardo Diego

Suzuki, Luciane Yumi

I am this author

Bassani, Irionson Antônio

I am this author

Torresi, Ricardo Diego

I am this author

DOI

10.5151/2594-5327-0456

Downloads

Abstract

Neste projeto está sendo investigada a relação entre a espessura da camada nitretada e revestida com TiAlN e as propriedades mecânicas da camada duplex. Na primeira etapa do projeto foram produzidas camadas nitretadas com 30, 60 e 90 μm em substrato de aço H13. As fases formadas na nitretação foram identificadas com auxílio de um difratômetro de raio X. As fases formadas nas três camadas nitretadas foram basicamente às mesmas, entretanto as camadas com 30 e 90 μm apresentaram picos referentes à camada de compostos com maior intensidade do que a amostra com 60 μm de espessura. Em uma segunda etapa realizou-se a deposição, por PAPVD, do revestimento de TiAlN nas amostras nitretadas. As camadas depositadas de TiAlN foram de 3,5 e 8 μm. As medidas de nanodureza realizadas nas superfícies com tratamento duplex revelaram que as amostras nitretadas e revestidas com 8 μm de TiAlN apresentaram dureza superior as amostras com 3,5 μm de TiAlN.

This study investigated the relation between nitriding thickness and TiAlN coating, and duplex layer mechanical properties. Samples were produced with 30um, 60um and 90um thick nitriding layer in H13 steel. The phases formed in nitriding were identified with X-ray diffraction. Basically, in the 30um, 60um and 90um samples the same phase was formed, but in the 30um and 90um samples we observed peaks related to the composites layer with more intensity than the 60um sample. After the nitriding, PAPVD TiAlN coating was deposited with two different thickness (3.5um and 8um). The nanoindentation hardness results in the duplex-treated samples showed that the samples with a 8um thickness coating had a bigger hardness than the 3.5um thickness coated samples.

Keywords

Nitretação; Dureza; Difração de raio-X; PAPVD; TiAlN.

Nitriding; Hardness; X-ray diffraction; PAPVD; TiAlN.