CARACTERIZAÇÃO DO RECOBRIMENTO DE NÍQUEL E FÓSFORO PARA AUMENTO DA RESISTÊNCIA AO DESGASTE DO AÇO CARBONO

CHARACTERIZATION OF NICKEL AND PHOSPHORUS COATING FOR INCREASED WEAR RESISTANCE OF CARBON STEEL

Authorship

Barros, Anne Muryel Resende; Moreira, Antônio Nereu; Sade, Wagner; Pinheiro, Ivete Peixoto

Barros, Anne Muryel Resende

I am this author

Moreira, Antônio Nereu

I am this author

Sade, Wagner

I am this author

Pinheiro, Ivete Peixoto

I am this author

DOI

10.5151/2594-5327-23267

Downloads

Abstract

Recobrimentos de níquel fósforo (NiP) são eficientes para aumento da resistência ao desgaste. Várias aplicações ocorrem nos setores de energia de petróleo e gás, minero-metalúrgico e a indústria têxtil. As propriedades físicas, mecânicas e a boa resistência à corrosão do revestimento NiP leva a substituição de algumas ligas especiais, como recobrimentos de cromo, que são prejudiciais à saúde. São muitas as variáveis que podem favorecer a resistência à abrasão e à corrosão desse revestimento: forma de deposição, teor de fósforo, adição de partículas duras e tratamento térmico realizado sobre a peça. A deposição do recobrimento de NiP sobre o aço carbono foi realizada por meio de processo químico autocatalítico, sem aplicação de corrente elétrica. Os corpos de prova foram recobertos com espessura aproximada de 28μm sobre placas de 50mm x 50mm x 3mm de aço carbono SAE 1020. A quantidade de fósforo contida no recobrimento NiP pesquisada foi o NP1(Ni - 8 ± 1%P) e NP2(Ni - 10±1%). Após as amostras serem submetidas a tratamentos térmicos, a dureza dos recobrimentos de NiP foi avaliada.

Nickel-phosphorus coatings (NiP) are effective for increasing wear resistance. Several applications occur in the energy of oil and gas, mining and metallurgical and textile industry. The physical, mechanical and corrosion resistance of the NiP coating leads to replacement of some special alloys such as chromium coatings which are detrimental to health. There are many variables that can promote corrosion and abrasion resistance of the coating: shape deposition, phosphorus, addition of hard particles and heat treatment carried out on the part. The deposition of the NiP coating on carbon steel was performed by autocatalytic chemical process, without the application of electric current. The specimens were covered with a thickness of 28+/-2mm on plates 50mm x 50mm x 3mm carbon steel SAE 1020. The amount of phosphorus contained in the NiP coatings searched was the NP1(Ni - 8 ± 1%P) and NP2(Ni - 10±1%). After being subjected to heat treatment, the microhardeness of NiP coatings were evaluated.

Keywords

Recobrimento NiP; Tratamento térmico; Resistência ao desgaste; Processo químico autocatalítico.

NiP coating; Heat treatment; Wear resistance; Autocatalytic chemical process.