CARACTERIZAÇÃO ESTRUTURAL DAS LIGAS Ti-18Si-6B E Ti-7,5Si-22,5B PROCESSADAS POR MOAGEM DE ALTA ENERGIA E PRENSAGEM A QUENTE

STRUCTURAL CHARACTERIZATION OF Ti-18Si-6B AND Ti-7.5Si-22.5B ALLOYS PROCESSED BY HIGH-ENERGY BALL MILLING AND HOT PRESSING

DOI

10.5151/2594-5327-0378

Downloads

Abstract

Este trabalho apresenta a preparação de ligas Ti-18Si-6B e Ti-7,5Si-22,5B (%-at.) por moagem de alta energia e subseqüente prensagem a quente, a partir de pós de alta pureza. A moagem foi realizada em um moinho Fritsch P-5 sob atmosfera de argônio, velocidade de 200 rpm, e com vasos/esferas de aço inoxidável. Os pós moídos sofreram pré-compactação por prensagem uniaxial, e em seguida prensagem uniaxial a quente sob vácuo para a obtenção de compactados. As transformações de fases ocorridas durante a moagem e após consolidação foram avaliadas com o auxílio de difração de raios X (DRX), microscopia eletrônica de varredura (MEV), e espectrometria por energia dispersiva (EDS). A DRX apresenta o desaparecimento de picos de silício nos difratogramas dos pós moídos, o que indica uma dissolução de átomos de silício e de boro na estrutura do titânio. Além disso, a existência de halos sugere a possibilidade de formação de estruturas amorfas nestes pós. Após prensagem a quente, as fases Ti+Ti6Si2B+Ti5Si3 e Ti+Ti6Si2B+TiB são identificadas nas ligas Ti-18Si-6B e Ti-7,5Si-22,5B (%-at.), respectivamente. Análises por EDS indicam teores de ferro inferiores a 6 %-p.

 

This work presents the Ti-18Si-6B and Ti-7.5Si-22.5B (at.-%) alloys preparation by high- energy ball milling and subsequent hot pressing from high-purity powders. The milling was carried out in a Fritsch P-5 mill under argon atmosphere, rotary speed of 200rpm, stainless steel vials/balls, and with a ball-to-powder weight ratio of 10:1. The milled powders were precompacted by uniaxial pressing, and subsequently consolidated by vacuum hot pressing in order to obtain bulks. The phase transformations during ball milling and after consolidation by hot pressing were evaluated by means of X-rays diffraction (XRD), scanning electron microscopy (SEM), and energy dispersive spectrometry (EDS). XRD experiments indicate that the silicon peaks disappear in the milled powders due to the silicon atoms dissolution into the titanium lattice. In addition, it is noted a halo formation during milling of the both powder mixtures. After hot pressing, peaks of Ti+Ti6Si2B+Ti5Si3 and Ti+Ti6Si2B+TiB are identified in Ti-18Si-6B and Ti-7.5Si-22.5B (at.-%) alloys, respectively. Iron contamination lower than 6 wt.-% was measured by EDS analysis.

Keywords

Moagem de alta energia; Ligas de titânio; Fase ternária.

High-energy ball milling; Titanium alloys; Ternary phases.

How to refer

Fernandes, Bruno Bacci; Ramos, Alfeu Saraiva; Neto, Carlos de Moura; Melo, Francisco Cristovão Lourenço de; Fernandes, Paulino Bacci. CARACTERIZAÇÃO ESTRUTURAL DAS LIGAS Ti-18Si-6B E Ti-7,5Si-22,5B PROCESSADAS POR MOAGEM DE ALTA ENERGIA E PRENSAGEM A QUENTE , p. 3477-3486. In: 62º Congresso anual da ABM, Vitória, 2007.