Title

CARACTERIZAÇÃO MICROESTRUTURAL E DA TEXTURA CRISTALOGRÁFICA DA LIGA AlAA1070 DEFORMADA A FRIO VIA PRENSAGEM EM CANAIS EQUIANGULARES

MICROSTRUCTURE ́S AND TEXTURE ́S CHARACTERIZATION OF THE AlAA1070 ALLOY COLD DEFORMED BY EQUAL CHANNEL ANGULAR PRESSING

Authorship

Rezende, Monica Costa; Abrantes, André Luiz de Andrade; Hauegen, Christien Guisard; Lins, Jefferson Fabrício Cardoso

Rezende, Monica Costa

I am this author

Abrantes, André Luiz de Andrade

I am this author

Hauegen, Christien Guisard

I am this author

Lins, Jefferson Fabrício Cardoso

I am this author

DOI

10.5151/2594-5300-20295

Downloads

Abstract

O objetivo deste trabalho foi promover o refinamento da microestrutura da liga de alumínio de pureza comercial AlAA1070, a qual foi submetida a DPS. O material foi prensado em canais equiangulares – ECAP. A amostra foi submetida a cinco passes pela rota Bc. O processamento ocorreu à temperatura ambiente e alcançou ε = 5,95. MEV e EBSD foram utilizados para analisar a evolução da microestrutura e da textura cristalográfica do material após cautelosa preparação metalográfica. Medidas de dureza Vickers foram realizadas para determinar a dureza após cada etapa de processamento. Após a deformação severa o material apresentou grãos ultrafinos exibindo textura com componentes de cisalhamento e a dureza se elevou consideravelmente. Com estes resultados pode-se concluir que os processos de subdivisão de grãos e recristalização dinâmica foram os responsáveis pelas alterações microestruturais e consequentemente na textura e no comportamento mecânico do material.

The objective was to promote the refinement of the microstructure of aluminum alloy Al AA1070 commercial purity, which was submitted to SPD. The material was pressed into channels equiangular - ECAP. The sample was subjected to five passes by route Bc. The processing occurred at room temperature and reached ε = 5.95. SEM and EBSD were used to analyze the evolution of the microstructure and crystallographic texture of the material after a careful metallographic preparation. Vickers hardness measurements were performed to determine the hardness after each processing step. After severe deformation the material presented showing ultrafine grain texture hardness and shear components rose considerably. With these results we can conclude that the processes of grain subdivision and dynamic recrystallization were responsible for the microstructural changes and consequently in texture and mechanical behavior of the material.

Keywords

Liga AlAA1070; DPS; ECAP; Refinamento microestrutural.

AlAA1070 alloy; SPD; ECAP; Microstructure refinement.