Title

CARACTERIZAÇÃO POR ANÁLISE DE IMAGENS DO EFEITO DE FLUXOS NA SOLDAGEM TIG

CHARACTERIZATION BY ANALYSIS OF IMAGES OF ACTIVATED FLUX EFFECT ON TIG WELDING

Authorship

Rodrigues, Felipe Gabriel Pinheiro; Gonçalves, Caroline Nazaré; Modenesi, Paulo José; Santos, Neice Ferreira dos

Rodrigues, Felipe Gabriel Pinheiro

I am this author

Gonçalves, Caroline Nazaré

I am this author

Modenesi, Paulo José

I am this author

Santos, Neice Ferreira dos

I am this author

DOI

10.5151/1516-392X-31408

Downloads

Abstract

Esse trabalho visa estudar, pela análise de imagens do arco, os mecanismos propostos para explicar o aumento de penetração na soldagem TIG quando é utilizado fluxo ativo na superfície (A-TIG). Foram realizados testes com fluxos de Cr2O3, SiO2 e TiO2 para avaliação da ocorrência de alterações na forma do arco que indiquem, por exemplo, a ocorrência de sua constrição. Para tal, foi feita a aquisição de dados de corrente e tensão, bem como fotografias do arco durante a soldagem com uma câmera semiprofissional e uma lente de macrografia, para que fosse possível uma melhor avaliação de quaisquer variações no arco no decorrer do teste. Foi notado um aumento da tensão quando utilizados Cr2O3 e SiO2 como fluxo, entretanto não foi observada variações consideráveis na largura do arco de soldagem, o que seria uma indicação de constrição elétrica do arco.

This paper aims to study, supported by images of the electric arc, the proposed systems to explain the increase of penetration in TIG welding when an active flux is used in the surface (A-TIG). Tests with Cr2O3, SiO2 and TiO2 were carried out to evaluate the occurrence of changes in the electric arc that could indicate, for example, an occurrence of its construction. A data acquisition system was used, to evaluate changes in current and voltage. Images of the arc were taken during the welding with a semiprofessional camera and a macrograph lens. This montage would be capable to better evaluate any changes in the plasma column. It was noticed an increase in the voltage when Cr2O3 and SiO2 were used as active flux. However was not noticed major variations in the electric arc width, what could indicate an electric constriction of the arc. It was not noticed any correlation between the increase in the arc voltage and it dimension changes.

Keywords

Soldagem A-TIG; Constrição do arco; Fotografia do arco; Sinais elétricos.

Activated Flux TIG Welding; Arc Constriction; Arc Photography; Electric signals