CARACTERIZAÇÃO TECNOLÓGICA DE UM REJEITO DE FLOTAÇÃO DE MINÉRIO DE LÍTIO

TECHNOLOGICAL CHARCACTERIZATION OF A TAILING FROM LITIUM ORE FLOTATION

Authorship

OLIVEIRA, RODRIGO CARNEIRO DE; SILVA, RAYKAR BANDEIRA; LIMA, ROSA MALENA FERNANDES

OLIVEIRA, RODRIGO CARNEIRO DE

I am this author

SILVA, RAYKAR BANDEIRA

I am this author

LIMA, ROSA MALENA FERNANDES

I am this author

DOI

10.5151/2594-5327-40628

Downloads

Abstract

NESTE TRABALHO FOI EFETUADA CARACTERIZAçõES FíSICA (DISTRIBUIçãO GRANULOMéTRICA POR PENEIRAMENTO, DETERMINAçãO DE MASSA ESPECíFICA POR PICNOMETRIA A GáS E áREA SUPERFICIAL ESPECíFICA POR BET); MINERALóGICA POR DIFRATOMETRIA DE RAIOS X E QUíMICA (FLUORESCêNCIA DE RAIOS X E ESPECTROSCOPIA óTICA DE EMISSãO ATôMICA COM PLASMA DE ACOPLAMENTO INDUTIVO) DE UMA AMOSTRA DE REJEITO DA ETAPA DE FLOTAçãO DE MINéRIO DE LI DE UMA EMPRESA DE MINERAçãO, LOCALIZADA NO CAMPO DAS VERTENTES-MG. PELA CURVA DE DISTRIBUIçãO GRANULOMéTRICA DA AMOSTRA VERIFICOU-SE QUE O P80 DA MESMA FOI DE 246,7 µM, MASSA ESPECíFICA IGUAL 2,72 G/CM3 E áREA SUPERFICIAL ESPECíFICA DE 0,45 M2/G. OS MINERAIS MAJORITáRIOS IDENTIFICADOS FORAM FELDSPATO (ALBITA E MICROCLINA), QUARTZO E MOSCOVITA. OS MINERAIS PORTADORES DE LI EM PROPORçõES MENORES FORAM O ESPODUMêNIO E A LEPDOLITA. PELOS RESULTADOS DA ANáLISE GRANULOQUíMICA VERIFICOU-SE MAIORES TEORES DE FE2O3 NA FRAçãO GANULOMéTRICA -75 µM EM RELAçãO COM FRAçãO GRANULOMéTRICA + 75 µM. O INVERSO OCORREU COM O TEOR DE LI2O. NO ENTANTO, COMO O TEOR GLOBAL DE FE2O3 FOI DE 0,23%, ESTE MATERIAL é DESTINADO PARA INDúSTRIA DE CERâMICA

IN THIS WORK, WERE CARRIED OUT CHARACTERIZATIONS PHYSICAL (PARTICLE SIZE DISTRIBUTION BY SIEVING, SPECIFIC MASS DETERMINATION BY GAS PYCNOMETRY AND SPECIFIC SURFACE AREA BY BET), MINERALOGICAL BY X-RAY DIFFRACTOMETRY AND CHEMICAL (X-RAY FLUORESCENCE AND OPTICAL SPECTROSCOPY OF ATOMIC EMISSION WITH INDUCTIVELY COUPLED PLASM) OF A TAILING SAMPLE FROM THE LI ORE FLOTATION STAGE OF A MINING COMPANY, LOCATED IN THE CAMPO DAS VERTENTES-MG. THE PARTICLE SIZE DISTRIBUTION CURVE OF THE SAMPLE SHOWED THAT ITS P80 WAS 246.7 µM, SPECIFIC MASS EQUAL TO 2.72 G/CM3 AND SPECIFIC SURFACE AREA OF 0.45 M2/G. THE MAJORITY MINERALS IDENTIFIED WERE FELDSPAR (ALBITE AND MICROCLINE), QUARTZ AND MUSCOVITE. THE LI-BEARING MINERALS IN SMALLER PROPORTIONS WERE SPODUMENE AND LEPDOLITE. THE RESULTS OF THE GRANULOCHEMICAL ANALYSIS SHOWED HIGHER GRADES OF FE2O3 IN THE -75 µM SIZE FRACTION COMPARED WITH SIZE FRACTION + 75 µM. THE OPPOSITE OCCURRED WITH THE LI2O. HOWEVER, AS THE OVERALL FE2O3 CONTENT WAS 0.23%, THIS MATERIAL IS INTENDED FOR THE CERAMICS INDUSTRY

Keywords

Minério de lítio; Espodumênio; Rejeito; Feldspato

Litium ore, spodumenium, Tailing; Feldspar