Title

COMPARAÇÃO ENTRE OS COMPORTAMENTOS DE FLUÊNCIA DO AÇO 1CR0.5MO NAS CONDIÇÕES VIRGEM E DETERIORADO EM SERVIÇO COM TESTES A CARGA E A TENSÃO CONSTANTES. PARTE 1: RELAÇÕES ENTRE TEMPO DE RUPTURA, TENSÃO E TEMPERATURA

CREEP BEHAVIOR OF 1CR0.5MO STEEL IN VIRGIN AND EX-SERVICE CONDITIONS WITH CONSTANT STRESS AND CONSTANT LOAD CREEP TESTS. PART1: RELATIONS AMONG RUPTURE TIME, STRESS AND TEMPERATURE

Authorship

BUENO, LEVI DE OLIVEIRA; SOBRINHO, JOSÉ FRANCISCO DOS REIS

BUENO, LEVI DE OLIVEIRA

38 Articles, Downloaded 234 Times

SOBRINHO, JOSÉ FRANCISCO DOS REIS

I am this author

DOI

10.5151/2594-5327-41638

Downloads

Abstract

ENSAIOS DE FLUêNCIA SOB CARGA CONSTANTE E SOB TENSãO CONSTANTES FORAM UTILIZADOS NO ESTUDO DO COMPORTAMENTO DE RESISTêNCIA DO AçO 1CR0.5MO EM DUAS CONDIçõES MICROESTRUTURAIS: NO ESTADO VIRGEM E NO ESTADO DETERIORADO APóS 15 ANOS DE OPERAçãO A UMA TEMPERATURA NOMINAL DE 550ºC. GRáFICOS DE QUEDA DE RESISTêNCIA COM O TEMPO DE RUPTURA FORAM LEVANTADOS NAS QUATRO DIFERENTES CONDIçõES DE ENSAIO, BEM COMO GRáFICOS DA VARIAçãO DO TEMPO DE RUPTURA COM O INVERSO DA TEMPERATURA PARA SE IDENTIFICAR OS VALORES DA CONSTANTE C VISANDO PARAMETRIZAçãO DOS DADOS PELO MéTODO DE LARSON-MILLER. AS QUATRO CURVAS PARAMéTRICAS DO MATERIAL SãO COMPARADAS ENTRE SI, OBSERVANDO-SE QUE OS RESULTADOS COM OS TESTES A TENSãO CONSTANTE TêM UMA TENDêNCIA A SUPERESTIMAR A RESISTêNCIA à RUPTURA DO MATERIAL EM RELAçãO AOS TESTES SOB CARGA CONSTANTE, PORéM COM TENDêNCIA DE CONVERGêNCIA DAS QUATRO CURVAS PARA VALORES CADA VEZ MAIS ALTOS DO PARâMETRO PLM. UM CáLCULO DA TENSãO ADMISSíVEL PARA USO DO MATERIAL DETERIORADO POR MAIS 15 ANOS DE SERVIçO A 550ºC INDICA VALORES DE 48 E 47 MPA, PARA OS ENSAIOS A TENSãO E CARGA CONSTANTES, RESPECTIVAMENTE.

CREEP TESTS UNDER CONSTANT LOAD AND CONSTANT STRESS WERE USED IN THE STUDY OF RUPTURE STRENGTH BEHAVIOR OF 1CR0.5MO STEEL IN TWO MICROSTRUCTURAL CONDITIONS: IN THE VIRGIN STATE AND IN THE EX-SERVICE CONDITION AFTER 15 YEAR OPERATION AT A NOMINAL TEMPERATURE OF 550°C.GRAPHS OR DROP OF STRENGTH WITH RUPTURE TIME WERE PLOTTED IN THE FOUR DIFFERENT TEST CONDITIONS, AS WELL AS GRAPHS OF THE VARIATION OF RUPTURE TIME WITH THE INVERSE OF TEMPERATURE TO THE IDENTIFY THE VALUES OF THE C CONSTANT FOR DATA PARAMETERIZATION USING THE LARSON-MILLER METHOD. THE FOUR PARAMETRIC CURVES OF THE MATERIAL ARE COMPARED WITH EACH OTHER, OBSERVING THAT THE RESULTS WITH TESTS AT CONSTANT STRESS HAVE A TENDENCY TO OVERESTIMATE THE RUPTURE STRENGTH OF THE MATERIAL IN RELATION TO TESTS UNDER CONSTANT LOAD, HOWEVER WITH A TREND FOR THE FOUR CURVES TO CONVERGE FOR INCREASING VALUES OF THE PLM PARAMETER. CALCULATION OF THE ALLOWABLE STRESS FOR USE OF THE DETERIORATED MATERIAL FOR A FURTHER 15 YEAR OF SERVICE AT 550°C INDICATES VALUES OF 48 AND 47 MPA FOR CONSTANT STRESS AND CONSTANT LOAD TESTS, RESPECTIVELY

Keywords

Ensaio Fuência Carga Constante; Ensaio Fluência Tensão Constante; Aço 1Cr0.5Mo; Parametrização L-M

Constant Load Creep test; Constant Stress Creep Test; 1CR0.5Mo Steel; Larson-Miller Parameterization