COMPARAÇÃO ENTRE OS COMPORTAMENTOS DE FLUÊNCIA DO AÇO 1CR0.5MO NAS CONDIÇÕES VIRGEM E DETERIORADO EM SERVIÇO COM TESTES A CARGA E A TENSÃO CONSTANTES. PARTE 2: RELAÇÕES ENTRE TAXA DE DEFORMAÇÃO, TENSÃO E TEMPERATURA

CREEP BEHAVIOR OF 1CR0.5MO STEEL IN THE VIRGIN AND EX-SERVICE CONDITIONS WITH CONSTANT STRESS AND CONSTANT LOAD CREEP TESTS. PART 2: RELATIONS AMONG MINIMUM CREEP RATE, STRESS AND TEMPERATURE

Authorship

BUENO, LEVI DE OLIVEIRA; SOBRINHO, JOSÉ FRANCISCO DOS REIS

BUENO, LEVI DE OLIVEIRA

I am this author

SOBRINHO, JOSÉ FRANCISCO DOS REIS

I am this author

DOI

10.5151/2594-5327-41650

Downloads

Abstract

ENSAIOS DE FLUêNCIA SOB CARGA CONSTANTE E SOB TENSãO CONSTANTES FORAM UTILIZADOS NO ESTUDO DO COMPORTAMENTO DA TAXA MíNIMA DE FLUêNCIA DO AçO 1CR0.5MO EM DUAS CONDIçõES MICROESTRUTURAIS: NO ESTADO VIRGEM E NO ESTADO DETERIORADO APóS 15 ANOS DE OPERAçãO A UMA TEMPERATURA NOMINAL DE 550ºC. GRáFICOS DA VARIAçãO DA TAXA MíNIMA DE FLUêNCIA COM A TENSãO FORAM LEVANTADOS NAS QUATRO DIFERENTES CONDIçõES DE ENSAIO, BEM COMO GRáFICOS DA TAXA MíNIMA DE FLUêNCIA COM O INVERSO DA TEMPERATURA PARA SE IDENTIFICAR OS VALORES DA ENERGIA DE ATIVAçãO APARENTE DE FLUêNCIA VISANDO PARAMETRIZAçãO DOS DADOS PELO MéTODO DE ZENER-HOLLOMON. AS QUATRO CURVAS PARAMéTRICAS DO MATERIAL LOG(Z)XLOG(TENSãO) SãO COMPARADAS ENTRE SI, OBSERVANDO-SE QUE OS RESULTADOS COM OS TESTES A TENSãO CONSTANTE TêM UMA TENDêNCIA A SUPERESTIMAR A RESISTêNCIA A FLUêNCIA DO MATERIAL EM RELAçãO AOS TESTES SOB CARGA CONSTANTE, PORéM COM TENDêNCIA DE CONVERGêNCIA DAS QUATRO CURVAS PARA VALORES CADA VEZ MAIS BAIXOS DA TENSãO. GRáFICOS DE MONKMAN-GRANT SãO TAMBéM APRESENTADOS PARA AS QUATRO CONDIçõES ESTUDADAS DO MATERIAL

CREEP TESTS UNDER CONSTANT LOAD AND CONSTANT STRESS WERE USED IN THE STUDY OF MINIMUM CREEP RATE BEHAVIOR OF 1CR0.5MO STEEL IN TWO MICROSTRUCTURAL CONDITIONS: IN THE VIRGIN STATE AND IN THE EX-SERVICE CONDITION AFTER 15 YEAR OPERATION AT A NOMINAL TEMPERATURE OF 550°C.GRAPHS OR DROP OF VARIATION OF MINIMUM CREEP RATE WITH STRESS WERE PLOTTED IN THE FOUR DIFFERENT TEST CONDITIONS, AS WELL AS GRAPHS OF THE VARIATION OF MINIMUM CREEP RATE WITH THE INVERSE OF TEMPERATURE TO THE IDENTIFY THE VALUES OF THE APPARENT CREEP ACTIVATION ENERGY FOR DATA PARAMETERIZATION USING THE ZENER-HOLLOMON METHOD. THE FOUR PARAMETRIC CURVES OF THE MATERIAL LOG(Z)XLOG(STRESS) ARE COMPARED WITH EACH OTHER, OBSERVING THAT THE RESULTS WITH TESTS AT CONSTANT STRESS HAVE A TENDENCY TO OVERESTIMATE THE CREEP STRENGTH OF THE MATERIAL IN RELATION TO TESTS UNDER CONSTANT LOAD, HOWEVER WITH A TREND FOR THE FOUR CURVES TO CONVERGE FOR INCREASINGLY LOWER VALUES OF STRESS. MONKMAN-GRANT GRAPHS ARE ALSO PRESENTED FOR THE FOUR STUDIED CONDITIONS OF THE MATERIAL

Keywords

Ensaio Fluência Carga Constante; Ensaio Fluência Tensão Constante; Aço 1Cr0.5Mo; Parametrização z-h

Constant Load Creep test; Constant Stress Creep Test; 1Cr0.5Mo Steel; Z-h parameterization