Title

COMPARATIVO DE UMA PASTA GEOPOLIMÉRICA DE METACAULIM E CINZA VOLANTE COM CURA AMBIENTE E TÉRMICA NAS IDADES INICIAIS

COMPARISON OF A GEOPOLIMER PASTE OF METAKAOLIN AND FLY ASH WITH ENVIRONMENTAL AND THERMAL CURING AT EARLY AGES

Authorship

OLIVEIRA, LEANDRO BARBOSA DE

OLIVEIRA, LEANDRO BARBOSA DE

I am this author

DOI

10.5151/2594-5327-40680

Downloads

Abstract

O CIMENTO PORTLAND é UM DOS MATERIAIS MAIS UTILIZADOS DO MUNDO. PORéM, A DEMANDA E O GASTO ENERGéTICO TêM ELEVADO A BUSCA POR MATERIAIS ALTERNATIVOS E MAIS SUSTENTáVEIS QUE POSSAM SUPRIR ESSA LACUNA. ASSIM, O OBJETIVO DESSA PESQUISA FOI DE REALIZAR UMA PASTA GEOPOLIMéRICA DE METACAULIM, SUBSTITUINDO PARCIALMENTE PELA CINZA VOLANTE EM PORCENTAGENS DE 20 E 40%, COM CURA AMBIENTE E A 65 ºC PARA REALIZAR OS ENSAIOS NO ESTADO ENDURECIDO DE RESISTêNCIA à COMPRESSãO E DENSIDADE APARENTE AOS 3 E 6 DIAS. OS RESULTADOS MOSTRARAM QUE A CURA TéRMICA ACELEROU O PROCESSO DE GEOPOLIMERIZAçãO E ALCANçOU RESULTADOS DE 12,71, 11,56 E 9,76 MPA PARA (0%, 20% E 40% DE CINZA VOLANTE) AOS 3 DIAS, ENQUANTO NA CURA AMBIENTE APENAS A AMOSTRA DE REFERêNCIA DE METACAULIM TEVE RESULTADOS SATISFATóRIOS, CHEGANDO A 11,32 MPA. PARA OS 6 DIAS, COM O TEMPO MAIOR PARA A ATIVAçãO ALCALINA, OS COMPOSTOS COM CURA AMBIENTE TIVERAM MELHORES RESULTADOS COMPARADOS AOS 3 DIAS, COM GANHOS DE 30,1%, 54,7% E 247% PARA (0%, 20% E 40% DE SUBSTITUIçãO). DESSA FORMA, OBSERVOU-SE QUE PARA AS IDADES INICIAIS, O GEOPOLíMERO DE METACAULIM E CINZA VOLANTE APRESENTA MAIOR POTENCIAL DE APLICAçãO QUANDO UTILIZADOS COM CURA TéRMICA EM TEMPERATURAS MODERADAS EM TORNO DE 60 ºC.

PORTLAND CEMENT IS ONE OF THE MOST USED MATERIALS IN THE WORLD. HOWEVER, DEMAND AND ENERGY EXPENDITURE HAVE INCREASED THE SEARCH FOR ALTERNATIVE AND MORE SUSTAINABLE MATERIALS THAT CAN FILL THIS GAP. THUS, THE OBJECTIVE OF THIS RESEARCH WAS TO CREATE A METAKAOLIN GEOPOLYMERIC PASTE, PARTIALLY REPLACING IT WITH FLY ASH IN PERCENTAGES OF 20 AND 40%, WITH CURING AT 25 AND 65 º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ºC.

Keywords

Geopolímero; Metacaulim; Cinza volante; Cura térmica; Resistência à compressão

Geopolymer; Metakaolin; Fly ash; Thermal curing; Compressive strength