Title

COMPORTAMENTO DA EROSÃO - OXIDAÇÃO DE AÇOS EM TEMPERATURAS ELEVADAS

HIGH TEMPERATURE EROSION-OXIDATION BEHAVIOR OF STEELS

Authorship

M.C.Fernandes, Stela; Correa, Olandir V.; Ramanathan, Lalgudi

M.C.Fernandes, Stela

I am this author

Correa, Olandir V.

I am this author

Ramanathan, Lalgudi

I am this author

DOI

10.5151/2594-5327-0042

Downloads

Abstract

Foram determinados os comportamentos da erosão – oxidação (E-O) dos aços AISI 1020, 304, 310, e 410. Estes aços foram selecionados para avaliar também o efeito do teor do cromo sobre a resistência E-O. Foi utilizado um aparato no qual um conjunto de corpos de prova foram sujeitos a rotação num leito de partículas erosivas fluidizadas. Foram utilizados pós de alumina (200μm) como partículas erosivas. Os ensaios de E-O foram realizados na faixa de temperatura de 25 - 600oC, com velocidade media de impacto das partículas de 3.5 a 15 ms-1 e com angulo de impacto de 90o. Desgaste E- O dos aços expostas a partículas com baixa velocidade de impacto estava baixo, mas aumentou com aumento em temperatura ate 300o C. O desgaste E-O dos diversos aços foi similar quando exposta a partículas erosivas a velocidade alta. O desgaste aumentou com aumento em temperatura acima de 500o C. O aumento em desgaste E- O, dependendo do aço, observados a temperaturas acima de 300o C, 400o C ou 500o C, foi devido a uma transição, de erosão para erosão – oxidação, no processo dominante de desgaste.

The high temperature erosion-oxidation (E-O) behavior of steels AISI 1020, 304, 310, and 410 were determined. These steels were selected to also evaluate the effect of chromium content on their E-O resistance. A test rig in which a specimen assembly was rotated through a fluidized bed of erodent particles was used to determine the E-O behavior. Alumina powder (200μm) was used as the erodent. The E-O tests were carried out in the temperature range 25 - 600oC, with average particle impact velocities of 3.5 and 15 ms-1 and impact angle of 90o. The E-O wastage of the steels exposed to low velocity particle impact was low but increased with temperature above 300o C. The E-O wastage of the different steels exposed to high velocity particle impact velocity was quite similar. The wastage increased with increase in temperature above 500o C. The increases in E-O wastage of the steels observed at temperatures above 300o C, 400o C or 500o C, depending on the steel, are due mainly to a transition in the dominant wastage process, from ‘erosion’ to ‘erosion-oxidation’.

Keywords

Oxidação; Erosão; Erosão-oxidação; Desgaste; Aços.

Oxidation; Erosion; Erosion-oxidation; Wastage; Steels.