COMPORTAMENTO DE CRISTALIZAÇÃO DOS FILMES DE PÓS FLUXANTES NO MOLDE DE LINGOTAMENTO CONTÍNUO

CRYSTALLIZATION OF MOULD FLUXES FILMS IN THE CONTINUOUS CASTING MOULD

Authorship

Oliveira, Leonardo José Silva de; Nascimento, André Afonso; Lima, Marco Túlio Dias; Tavares, Roberto Parreiras

Oliveira, Leonardo José Silva de

I am this author

Nascimento, André Afonso

I am this author

Lima, Marco Túlio Dias

I am this author

Tavares, Roberto Parreiras

I am this author

DOI

10.5151/2594-5300-15908

Downloads

Abstract

A cristalização dos pós fluxantes é muito importante para o processo de solidificação do aço. Ele se solidifica na interface entre a placa e o molde e é responsável pela lubrificação e principalmente pela transferência de calor. Os filmes de pó fluxante podem ser vítreos, cristalinos ou uma mistura de ambos, sendo a fase cristalina predominante a cuspidina (Ca4SiO7F2). A formação de fases cristalinas é uma questão cinética envolvendo principalmente mecanismos de nucleação e crescimento de fases. Neste trabalho visou-se avaliar a quantidade de fase cristalina presente em um filme de pó fluxante solidificado em laboratório utilizando técnicas de Análise Térmica Diferencial (ATD). Estas técnicas foram comparadas com observações microestruturais e difração de raios-X.

The mould fluxes crystallization is very important for the continuous casting process. The melt mould fluxes will solidify when they infiltrate into the gap, formed between the mould and the slab, and it must promote the lubrication and better heat transference. The mould fluxes films can be totally glassy, crystalline or both. The most common crystalline phase formed during solidification of mould powder with additions of fluorite is cuspidine (Ca4SiO7F2). The formation of crystalline phases is carried out to nucleation and growth kinetics mechanisms. The aim of this study was to evaluate the amount of crystalline phase in solidified mould fluxes films using laboratory apparatus. The differential thermo analysis (DTA) and X-ray diffraction (DRX) were used to determinate the presents phases in the solidified films. The results obtained with these two different techniques were compared with microscopic observations.

Keywords

Pó fluxante; Cristalização; Lingotamento contínuo

Mould fluxes; Crystallization; Continuous casting