COMPORTAMENTO DE RESULTADOS NA VARIAÇÃO DE ESPESSURA ENTRE ENSAIO E SIMULAÇÃO DO LATÃO 70/30 LAMINADO A FRIO NO MODO NAKAZIMA EM MÁQUINA DE ENSAIOS DE FITAS E CHAPAS

BEHAVIOR COMPARATIVE STUDY BETWEEN RESULTS OBTAINED TEST AND SIMULATION OF THE 70-30 BRASS COLD ROLLING IN THE NAKAZIMA MODE OF THE SHEET AND STRIP METAL TEST MACHINE

DOI

10.5151/2594-5297-17620

Downloads

Abstract

Estudou-se as diferenças de comportamento para a variação de espessura entre o ensaio, simulação e teoria pelo método Nakazima de fitas com 0,25 mm de espessura do latão 70/30 ou UNS C26000, liga composta de 70%Cu-30%Zn, muito aplicada em estampagem de cartuchos e que requer grande estampabilidade. No ensaio Nakazima as variações ou deformações planares e de espessura foram realizadas por um punção semi-esférico e os resultados destas deformações foram obtidos por medição direta da malha de deformação com auxilio de software e imagens e a espessura com o auxilio do dispositivo de medição. Os parâmetros aplicados no caso real e características mecânicas serviram para alimentar tanto o banco de dados do software como os modelos teóricos. Os modelos virtuais dos corpos de prova Nakazima foram submetidos a condições semelhantes das aplicadas no ensaio físico. O comportamento dos corpos de prova real e virtual bem como, sua variação de espessura apresentou grande proximidade de resultados. As espessuras e as regiões de escoamento ficaram em posições muito próximas apesar do fator atrito não ter sido isolado. A simulação apresentou resultados próximos aos reais e representa em muito as condições reais.

 

In this article we studied the differences in behavior for the variation in thickness between the simulation and test based theory method Nakazima of tape with 0.25 mm thickness brass 70/30 or UNS C26000, alloy composed of 70% Cu-30% Zn, planar and thickness were performed by a semi-spherical punch and the results of these much applied in printing cartridges and requires great formability. In the trial Nakazima variations or deformations of strains were obtained by direct measurement of mesh deformation with the aid of software and images and thickness with the aid of the measuring device. The parameters applied in the real case and mechanical characteristics served to enter data in both the database software as the theoretical models. The virtual models of the specimens Nakazima were subjected to similar conditions applied in the physical testing. The behavior of the specimens real and virtual as well as its thickness variation showed close proximity of results. The thickness and drain regions were in locations very close despite the friction factor was not isolated. The simulation showed results similar to those in very real and represents the actual conditions.

Keywords

Nakazima; Afinamento de parede; Curva limite de conformação; AutoForm; Latão cartucho Máquina de ensaio Erichsen.

Nakazima; Forming limit curve; AutoForm; Cartridge brass; Erichsen test machine.

How to refer

Filho, André Ferrus; Rubio, Fábio; Tamashiro, Nilson Yukihiro; Dechechi, Rubens Wolney; Filho, Antenor Ferreira; Costa, Valdir. COMPORTAMENTO DE RESULTADOS NA VARIAÇÃO DE ESPESSURA ENTRE ENSAIO E SIMULAÇÃO DO LATÃO 70/30 LAMINADO A FRIO NO MODO NAKAZIMA EM MÁQUINA DE ENSAIOS DE FITAS E CHAPAS , p. 866-878. In: 47º Seminário de Laminação Processos e Produtos Laminados e Revestidos, Rio de Janeiro, 2010.