Title

COMPORTAMENTO ELETROQUÍMICO DO AÇO AUSTENÍTICO 316L EM PRESENÇA DE ÍONS CLORETO

ELECTROCHEMICAL BEHAVIOR OF AUSTENITIC STAINLESS STEEL 316L IN THE PRESENCE OF CHLORIDE IONS

Authorship

RIBEIRO, KÉSIA SIMÕES; REIS, TAMARA DA SILVA TAVARES DOS; SOARES, FRANCIELLY MOURA DE SOUZA; VASCONCELOS, RAFAEL DE ALMEIDA; ELIAS, CARLOS NELSON

RIBEIRO, KÉSIA SIMÕES

I am this author

REIS, TAMARA DA SILVA TAVARES DOS

I am this author

SOARES, FRANCIELLY MOURA DE SOUZA

I am this author

VASCONCELOS, RAFAEL DE ALMEIDA

I am this author

ELIAS, CARLOS NELSON

I am this author

DOI

10.5151/2594-5327-40999

Downloads

Abstract

O AçO INOXIDáVEL 316L é AMPLAMENTE EMPREGADO NAS INDúSTRIAS QUíMICAS E PETROQUíMICAS, DEVIDO à RESISTêNCIA MECâNICA E à CORROSãO. SUA NOTáVEL RESISTêNCIA à CORROSãO é ATRIBUíDA à FORMAçãO DE UMA CAMADA DE óXIDO PASSIVA. NO ENTANTO, EM AMBIENTES ALTAMENTE CORROSIVOS, COMO OS CONTENDO íONS CLORETO ASSOCIADOS A MEIOS áCIDOS, A RESISTêNCIA à CORROSãO DESTE MATERIAL PODE SER COMPROMETIDA. O PRESENTE ESTUDO TEVE COMO OBJETIVO COMPARAR A INFLUêNCIA DE DIFERENTES MEIOS NA RESISTêNCIA à CORROSãO DO AçO INOXIDáVEL 316L. FORAM REALIZADOS ENSAIOS ELETROQUíMICOS DE MEDIDA DE POTENCIAL DE CIRCUITO ABERTO E POLARIZAçãO POTENCIODINâMICA, UTILIZANDO AS SOLUçõES DE 3,5% DE NACL E 3,5% DE HCL. OS RESULTADOS MOSTRARAM QUE O MEIO áCIDO é MAIS CORROSIVO, EVIDENCIADO PELO DESLOCAMENTO DO POTENCIAL DE CIRCUITO ABERTO (OCP) E DO POTENCIAL DE CORROSãO PARA VALORES MENOS NOBRES, ACOMPANHADO DE UMA ALTA DENSIDADE DE CORRENTE DE CORROSãO. OS RESULTADOS ELETROQUíMICOS FORAM CORROBORADOS PELA INTENSA CORROSãO POR PITES NA AMOSTRA E PELA FORMAçãO DE PRODUTOS DE CORROSãO NA SOLUçãO.

STAINLESS STEEL 316L (SS 316L) IS WIDELY USED IN CHEMICAL AND PETROCHEMICAL INDUSTRIES DUE TO ITS FAVORABLE MECHANICAL STRENGTH, WELDABILITY, AND CORROSION RESISTANCE. ITS REMARKABLE CORROSION RESISTANCE IS ATTRIBUTED TO THE FORMATION OF A PASSIVE CHROMIUM OXIDE LAYER. HOWEVER, IN HIGHLY CORROSIVE ENVIRONMENTS, SUCH AS THOSE CONTAINING CHLORIDE IONS ASSOCIATED WITH ACIDIC MEDIA, THE CORROSION RESISTANCE OF THIS MATERIAL MAY BE COMPROMISED. THE PRESENT STUDY ANALYZED THE INFLUENCE OF ENVIRONMENT IN THE SS 316L CORROSION RESISTANCE. ELECTROCHEMICAL TESTS WERE CONDUCTED TO MEASURE OPEN CIRCUIT POTENTIAL AND POTENTIODYNAMIC POLARIZATION IN SOLUTIONS OF 3.5% NACL AND 3.5% HCL. THE RESULTS SHOWED THAT THE ACIDIC MEDIUM WAS THE MOST CORROSIVE, EVIDENCED BY THE DISPLACEMENT OF OPEN CIRCUIT POTENTIAL (OCP) AND CORROSION POTENTIAL TO LESS NOBLE VALUES, ACCOMPANIED BY A HIGH CORROSION CURRENT DENSITY. THE ELECTROCHEMICAL RESULTS WERE CONFIRMED BY THE INTENSE PITTING CORROSION ON THE SS 316L AND THE FORMATION OF CORROSION PRODUCTS IN THE SOLUTION.

Keywords

Corrosão; Aço Inoxidável 316L; Meio Ácido; Íons Cloreto.

Corrosion; Stainless Steel 316L; Acidic Environment; Chloride Ions.