CREEP-FATIGUE BEHAVIOR OF THE 9CR STEEL WITH W AND TA ADDITION

Authorship

BRASILEIRO, MARIA LUIZA WEDDERHOFF; GARCIA, JULIANNA MAGALHÃES; SOUSA, TALITA GAMA DE; NASCIMENTO, MARVIN DO; BRANDÃO, LUIZ PAULA MENDONÇA

BRASILEIRO, MARIA LUIZA WEDDERHOFF

I am this author

GARCIA, JULIANNA MAGALHÃES

I am this author

SOUSA, TALITA GAMA DE

I am this author

NASCIMENTO, MARVIN DO

I am this author

BRANDÃO, LUIZ PAULA MENDONÇA

I am this author

DOI

10.5151/2594-5327-41184

Downloads

Abstract

COM O INCREMENTO DA NECESSIDADE INDUSTRIAL DE USO DE MATERIAIS COM PROPRIEDADES MECâNICAS CADA VEZ MELHORES, TORNA-SE IMPORTANTE O ESTUDO DO COMPORTAMENTO DE LIGAS MODIFICADAS EM DIFERENTES CONDIçõES DE ENSAIO, UMA VEZ QUE é INDISPENSáVEL A COMPREENSãO DO COMPORTAMENTO DESSES DIFERENTES MATERIAIS EM DETERMINADOS AMBIENTES DE APLICAçãO. O PRESENTE ARTIGO TEVE COMO OBJETIVO ANALISAR O AçO 9CR MODIFICADO COM A ADIçãO DE W E TA QUANDO SUBMETIDO à FLUêNCIA-FADIGA. A PARTIR DO ESTUDO FOI POSSíVEL PERCEBER CARACTERíSTICAS DúCTEIS E FRáGEIS NAS AMOSTRAS, MESMO COM DIFERENTES TEMPOS DE EXPOSIçãO àS CONDIçõES DE FLUêNCIA. COM AS IMAGENS PRODUZIDAS POR UM INSTRUMENTO DE MICROSCOPIA ELETRôNICA DE VARREDURA, FEZ-SE A ANáLISE DA SUPERFíCIE DE FRATURA DAS AMOSTRAS, DE FORMA A CONSTATAR A EXISTêNCIA DE TRINCAS SECUNDáRIAS E AS VARIAçõES NO MODO DE FRATURA. FOI VERIFICADA UMA FRAGILIZAçãO DO MATERIAL COM O AUMENTO DO TEMPO DE EXPOSIçãO E DO TEMPO DE RETENçãO DA CARGA, PORéM COM A MANUTENçãO DE CERTO GRAU DE DUCTILIDADE.

WITH THE INCREASING INDUSTRIAL NEED FOR MATERIALS WITH IMPROVED MECHANICAL PROPERTIES, IT BECOMES IMPORTANT TO STUDY THE BEHAVIOR OF MODIFIED ALLOYS UNDER DIFFERENT TESTING CONDITIONS, AS UNDERSTANDING THE BEHAVIOR OF THESE DIFFERENT MATERIALS IN SPECIFIC APPLICATION ENVIRONMENTS IS ESSENTIAL. THIS ARTICLE AIMED TO ANALYZE 9CR STEEL MODIFIED WITH THE ADDITION OF W AND TA WHEN SUBJECTED TO CREEP-FATIGUE. FROM THE STUDY, IT WAS POSSIBLE TO OBSERVE BOTH DUCTILE AND BRITTLE CHARACTERISTICS IN THE SAMPLES, EVEN WITH DIFFERENT EXPOSURE TIMES TO CREEP CONDITIONS. USING IMAGES PRODUCED BY A SCANNING ELECTRON MICROSCOPE, THE FRACTURE SURFACE OF THE SAMPLES WAS ANALYZED TO CONFIRM THE EXISTENCE OF SECONDARY CRACKS AND VARIATIONS IN THE FRACTURE MODE. IT WAS FOUND THAT THE MATERIAL BECAME MORE BRITTLE WITH INCREASED EXPOSURE TIME AND LOAD HOLD TIME, ALTHOUGH IT MAINTAINED A CERTAIN DEGREE OF DUCTILITY.

Keywords

9Cr; W; Ta; Fluência-fadiga

9Cr; W; Ta; Creep-fatigue