Title

COMPORTAMENTO EM FLUÊNCIA E FADIGA DO AÇO AISI 310 COM ADIÇÃO DE N E NB

CREEP AND FATIGUE BEHAVIOR OF AISI 310 STEEL WITH N AND NB ADDITION

Authorship

BRASILEIRO, MARIA LUIZA WEDDERHOFF; GARCIA, JULIANNA MAGALHÃES; NASCIMENTO, MARVIN DO; SOUSA, TALITA GAMA DE; BRANDÃO, LUIZ PAULO MENDONÇA

BRASILEIRO, MARIA LUIZA WEDDERHOFF

I am this author

GARCIA, JULIANNA MAGALHÃES

I am this author

NASCIMENTO, MARVIN DO

I am this author

SOUSA, TALITA GAMA DE

I am this author

BRANDÃO, LUIZ PAULO MENDONÇA

I am this author

DOI

10.5151/2594-4711-41183

Downloads

Abstract

COM O DESENVOLVIMENTO DE NOVAS LIGAS METáLICAS, COM DIFERENTES COMPOSIçõES QUíMICAS PARA UMA MESMA FAMíLIA DE AçOS, COMO O AçO AISI 310, TORNA-SE IMPORTANTE O ESTUDO DO COMPORTAMENTO DESSES MATERIAIS EM DIFERENTES CONDIçõES DE TESTE, UMA VEZ QUE é NECESSáRIO SABER COMO REAGIRá A DETERMINADOS AMBIENTES DE APLICAçãO. O PRESENTE ARTIGO TEVE COMO OBJETIVO ANALISAR COMO O NOVO AçO AISI NBN SE COMPORTA QUANDO SUBMETIDO à FLUêNCIA E à FADIGA. A PARTIR DO ESTUDO, FOI POSSíVEL PERCEBER AS MUDANçAS DúCTEIS-FRáGEIS DO AçO, COM DIFERENTES TEMPOS DE EXPOSIçãO àS CONDIçõES DE FLUêNCIA. COM O USO DE UM INSTRUMENTO DE MICROSCOPIA ELETRôNICA DE VARREDURA, FOI POSSíVEL ANALISAR A SUPERFíCIE DE FRATURA DAS AMOSTRAS, DE FORMA A PERCEBER A EXISTêNCIA DE TRINCAS SECUNDáRIAS E MUDANçA DE MODO DE FRATURA. FOI VERIFICADA UMA FRAGILIZAçãO DO MATERIAL COM O AUMENTO DO TEMPO DE EXPOSIçãO E DO TEMPO DE RETENçãO DA CARGA.

WITH THE DEVELOPMENT OF NEW METALLIC ALLOYS, FEATURING DIVERSE CHEMICAL COMPOSITIONS WITHIN THE SAME STEEL FAMILY, SUCH AS AISI 310 STEEL, STUDYING THE BEHAVIOR OF THESE MATERIALS UNDER VARIOUS TESTING CONDITIONS BECOMES CRUCIAL, AS IT'S NECESSARY TO UNDERSTAND HOW THEY WILL REACT IN SPECIFIC APPLICATION ENVIRONMENTS. THIS ARTICLE AIMS TO ANALYZE THE BEHAVIOR OF THE NEW AISI NBN STEEL WHEN SUBJECTED TO CREEP AND FATIGUE. THROUGH THIS STUDY, DUCTILE-TO-BRITTLE CHANGES IN THE STEEL WERE OBSERVED WITH VARYING EXPOSURE TIMES TO CREEP CONDITIONS. UTILIZING SCANNING ELECTRON MICROSCOPY, THE FRACTURE SURFACES OF THE SAMPLES WERE ANALYZED, REVEALING THE PRESENCE OF SECONDARY CRACKS AND CHANGES IN FRACTURE MODE. MATERIAL EMBRITTLEMENT WAS OBSERVED WITH INCREASING EXPOSURE AND LOAD RETENTION TIMES.

Keywords

AISI 310, Nb, Fluência, N

AISI 310, Nb, Creep, N