COMPORTAMENTO MEC NICO DE TRAÇÃO EM COMPÓSITOS POLIMÉRICOS REFORÇADOS COM FIBRA DE ENVIRA CHEIROSA (ANNONA PALUDOSA AUBL.)

MECHANICAL TENSILE BEHAVIOR OF POLYMER COMPOSITES REINFORCED WITH ENVIRA CHEIROSA FIBER (ANNONA PALUDOSA AUBL.)

Authorship

MONTEIRO, MANOEL VINICIUS FRANCA; FERNANDES, JENNIFER FERREIRA; LIMA, HAIANNY BEATRIZ SARAIVA; SOUSA, ANA PAULA SOUZA DE; ESTUMANO, DIEGO CARDOSO; RODRIGUES, EMERSON CARDOSO; COSTA, DEIBSON SILVA DA

MONTEIRO, MANOEL VINICIUS FRANCA

32 Articles, Downloaded 167 Times

FERNANDES, JENNIFER FERREIRA

I am this author

LIMA, HAIANNY BEATRIZ SARAIVA

I am this author

SOUSA, ANA PAULA SOUZA DE

I am this author

ESTUMANO, DIEGO CARDOSO

I am this author

RODRIGUES, EMERSON CARDOSO

I am this author

COSTA, DEIBSON SILVA DA

I am this author

DOI

10.5151/2594-4711-40867

Downloads

Abstract

O INTERESSE GLOBAL EM TECNOLOGIAS SUSTENTáVEIS TEM DESTACADO OS DESAFIOS RELACIONADOS AO ACúMULO DOS PLáSTICOS SINTéTICOS. NESSE SENTIDO, UMA POSSíVEL SOLUçãO é A BUSCA POR NOVOS COMPóSITOS POLIMéRICOS REFORçADOS COM FIBRAS VEGETAIS, COMO AS ENCONTRADAS NA AMAZôNIA. DESSA FORMA, ESTE ESTUDO OBJETIVOU A CARACTERIZAçãO E VIABILIDADE DE COMPóSITOS COM FIBRAS DE ENVIRA CHEIROSA (ANNONA PALUDOSA AUBL.), UMA PLANTA Já UTILIZADA POR COMUNIDADES RURAIS NA CONSTRUçãO DE PAREDES DE CASAS DE TAIPA, PORéM AINDA POUCO EXPLORADA NA LITERATURA. A PRODUçãO DO COMPóSITO SEGUIU O MéTODO DE FABRICAçãO MANUAL HAND LAY-UP, COM MOLDE DE SILICONE, E INCORPORAçãO DE 1, 3 E 5% EM MASSA DA FIBRA, SEGUIDA DE COMPRESSãO COM 39 N. NA MATRIZ, UTILIZOU-SE A RESINA POLIéSTER ORTOFTáLICA INSATURADA E INICIADOR BUTANOX M-50 NA PROPORçãO 1% (V/V). FOI UTILIZADO O MéTODO DO PICNôMETRO PARA OBTENçãO DA MASSA ESPECíFICA DA FIBRA E NA CARACTERIZAçãO MORFOLóGICA, FOI UTILIZADA A MICROSCOPIA ELETRôNICA DE VARREDURA (MEV). PARA ANáLISE MECâNICA FOI UTILIZADA A NORMA ASTM D638 PARA OBTENçãO DOS RESULTADOS DE RESISTêNCIA à TRAçãO. A CARACTERIZAçãO MORFOLóGICA DEMONSTROU UMA FIBRA PREDOMINANTEMENTE LISA E OS ENSAIOS MECâNICOS DEMONSTRARAM UM AUMENTO SIGNIFICATIVO NA RESISTêNCIA à TRAçãO COM A ADIçãO DAS FIBRAS NA MATRIZ. INDICANDO, PORTANTO, QUE AS FIBRAS DE ENVIRA CHEIROSA TêM POTENCIAL COMO REFORçO EM COMPóSITOS, EM ESPECIAL NAS APLICAçõES QUE DEMANDAM MATERIAIS MAIS LEVES E RESISTENTES.

THE GLOBAL INTEREST IN SUSTAINABLE TECHNOLOGIES HAS BROUGHT ATTENTION TO THE CHALLENGES RELATED TO THE ACCUMULATION OF SYNTHETIC PLASTICS. IN THIS REGARD, A POSSIBLE SOLUTION IS THE PURSUIT OF NEW POLYMER COMPOSITES REINFORCED WITH PLANT FIBERS, SUCH AS THOSE FOUND IN THE AMAZON. THEREFORE, THIS STUDY AIMED TO CHARACTERIZE AND ASSESS THE FEASIBILITY OF COMPOSITES WITH FIBERS FROM THE ENVIRA CHEIROSA PLANT (ANNONA PALUDOSA AUBL.), A PLANT ALREADY USED BY RURAL COMMUNITIES IN THE CONSTRUCTION OF MUD HOUSE WALLS, YET STILL UNDEREXPLORED IN THE LITERATURE. THE PRODUCTION OF THE COMPOSITE FOLLOWED THE HAND LAY-UP MANUAL MANUFACTURING METHOD, USING A SILICONE MOLD, AND INCORPORATION OF 1, 3, AND 5% BY MASS OF FIBER, FOLLOWED BY COMPRESSION WITH 39 N. IN THE MATRIX, UNSATURATED ORTHOPHTHALIC POLYESTER RESIN AND 1% (V/V) BUTANOX M-50 INITIATOR WERE USED. THE PICNOMETER METHOD WAS USED TO OBTAIN THE SPECIFIC MASS OF THE FIBER, AND FOR MORPHOLOGICAL CHARACTERIZATION, SCANNING ELECTRON MICROSCOPY (SEM) WAS EMPLOYED. MECHANICAL ANALYSIS WAS CONDUCTED USING ASTM D638 STANDARD TO OBTAIN THE TENSILE STRENGTH RESULTS. MORPHOLOGICAL CHARACTERIZATION SHOWED PREDOMINANTLY SMOOTH FIBERS, AND MECHANICAL TESTS DEMONSTRATED A SIGNIFICANT INCREASE IN TENSILE STRENGTH WITH THE ADDITION OF FIBERS TO THE MATRIX. THUS, INDICATING THAT ENVIRA CHEIROSA FIBERS HAVE POTENTIAL AS REINFORCEMENT IN COMPOSITES, ESPECIALLY IN APPLICATIONS REQUIRING LIGHTER AND STRONGER MATERIALS.

Keywords

Matriz Poliéster; Compósitos Sustentáveis; Fibras da Amazônia.

Polyester Matrix; Sustainable Composites; Amazônia Fibers.