COMPORTAMENTO MECÂNICO DE LIGAS Cu-Al-Ni MONOCRISTALINA E POLICRISTALINA COM EFEITO DE MEMÓRIA DE FORMA

MECHANICAL BEHAVIOR OF MONOCRYSTALLINE AND POLYCRYSTALLINE Cu-Al-Ni ALLOYS EXHIBITING SHAPE MEMORY

Authorship

Leite, Vanessa Félix; Pereira, Elaine Cristina; Matlakhov, Anatoliy Nikolaevich; Matlakhova, Lioudmila Aleksandrovna; Araújo, Carlos José de; Almeida, Luciana Lezira Pereira de

Leite, Vanessa Félix

I am this author

Pereira, Elaine Cristina

I am this author

Matlakhov, Anatoliy Nikolaevich

I am this author

Matlakhova, Lioudmila Aleksandrovna

I am this author

Araújo, Carlos José de

I am this author

Almeida, Luciana Lezira Pereira de

I am this author

DOI

10.5151/2594-5327-14756

Downloads

Abstract

No presente trabalho foram estudadas as ligas monocristalina Cu-13,7%Al-4,2%Ni e policristalina Cu-13,7%Al-4%Ni, que exibem transformações martensíticas reversíveis. A liga monocristalina foi fabricada pelo "Memory Crystals Group", na Rússia, enquanto que a policristalina foi produzida no Brasil. Na caracterização destas ligas no estado como recebido, foram envolvidas as análises por espectroscopia de emissão atômica, difração de raios X, calorimetria diferencial de varredura, resistência elétrica e microscopia ótica. As amostras foram submetidas à deformação por compressão até atingir a fratura, utilizando a máquina INSTRON modelo 5582, à temperatura ambiente. A superfície de fratura foi avaliada por microscopia eletrônica de varredura. As análises mostraram que embora as ligas possuam composição química, estrutura e temperaturas críticas comparáveis, apresentam comportamento mecânico e superfície de fratura bem distintos.

In this work, monocrystalline and polycrystalline Cu-Al-Ni alloys exhibiting reversible martensitic transformation were studied. The monocrystalline alloy was produced by the firm "Memory Crystals Group", in Russia and polycrystalline alloy was produced in Brazil. Spectroscopy of atomic emission, X-ray diffraction, differential scanning calorimetry, electric resistance and optical microscopy analyses were used to characterize the alloys as received. The compressive deformation tests until the fracture were performed in specimens at room temperature in a 5582 INSTRON model machine. The fracture surface was analyzed by scanning electron microscopy. Analyses showed that although the alloys possess comparable chemical composition, structure and critical temperatures, they present different mechanical behavior and fracture surface.

Keywords

Ligas Cu-Al-Ni; Monocristais e policristais; Transformações martensíticas reversíveis; Comportamento mecânico.

Cu-Al-Ni alloy; Monocrystals and polycrystals; Reversible martensitic transformations; Mechanical behavior.